- 密度 [g/cm3]: 1.136
- 吸水率 [%]: 1.1
- 缺口冲击强度: 1.07
- 弯曲强度 [MPa]: 125.0
- 弯曲模量 [MPa]: 5.13
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.136 g/cc | 0.04104 lb/in³ | Melt; ISO 1183 | ||
| 1.39 g/cc | 0.0502 lb/in³ | dry; ISO 1183 | |||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 6.4 % | 6.4 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | 0.2 in/min; ASTM Test | ||
| 60.0 MPa @Temperature 120 °C | 8700 psi @Temperature 248 °F | ISO Data | |||
| 60.0 MPa @Temperature 120 °C | 8700 psi @Temperature 248 °F | ASTM Test | |||
| 80.0 MPa @Temperature 80.0 °C | 11600 psi @Temperature 176 °F | ASTM Test | |||
| 80.0 MPa @Temperature 80.0 °C | 11600 psi @Temperature 176 °F | ISO Data | |||
| 255 MPa @Temperature -40.0 °C | 37000 psi @Temperature -40.0 °F | ASTM Test | |||
| 255 MPa @Temperature -40.0 °C | 37000 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 125 MPa | 18100 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 6.0 % | 6.0 % | 5mm/min; ISO 527 | ||
| 6.0 % | 6.0 % | 0.2 in/min; ASTM Test | |||
| 3.5 % @Temperature -40.0 °C | 3.5 % @Temperature -40.0 °F | ASTM Test | |||
| 3.5 % @Temperature -40.0 °C | 3.5 % @Temperature -40.0 °F | ISO Data | |||
| 6.0 % @Temperature 120 °C | 6.0 % @Temperature 248 °F | ISO Data | |||
| 6.0 % @Temperature 80.0 °C | 6.0 % @Temperature 176 °F | ISO Data | |||
| 6.0 % @Temperature 120 °C | 6.0 % @Temperature 248 °F | ASTM Test | |||
| 6.0 % @Temperature 80.0 °C | 6.0 % @Temperature 176 °F | ASTM Test | |||
| Tensile Modulus | 5.84 GPa | 847 ksi | 1mm/min; ISO 527 | ||
| 3.40 GPa @Temperature 120 °C | 493 ksi @Temperature 248 °F | ISO Data | |||
| 4.30 GPa @Temperature 80.0 °C | 624 ksi @Temperature 176 °F | ISO Data | |||
| 11.6 GPa @Temperature -40.0 °C | 1680 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 130 MPa | 18900 psi | ISO Data | ||
| 179 MPa | 26000 psi | ASTM Test | |||
| 361 MPa @Temperature -40.0 °C | 52400 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 5.13 GPa | 744 ksi | ASTM Test | ||
| 5.20 GPa | 754 ksi | ISO Data | |||
| Izod Impact, Notched | 1.07 J/cm @Temperature -40.0 °C | 2.00 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 2.35 J/cm @Thickness 3.17 mm | 4.40 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 2.434 J/g-°C | 0.5817 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.275 W/m-K | 1.91 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||