- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 拉伸强度 [MPa]: 85.0
- 弯曲模量 [MPa]: 2.80
- 硬度: 120.0
- 热变形温度 [℃]: 160.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hour; ISO Test | ||
| 9.3 % | 9.3 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | ASTM Test | ||
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | 10 % | 10 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 3.50 GPa | 508 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 95.0 MPa | 13800 psi | ISO Data | ||
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO Data | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 81.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 45.0 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 | ||
| Flammability, UL94 | V-2 @Thickness 0.700 mm | V-2 @Thickness 0.0276 in | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| UL.UL-C | Yes | ||||