- 密度 [g/cm3]: 1.289
- 吸水率 [%]: 0.9
- 缺口冲击强度: 0.55
- 弯曲强度 [MPa]: 115.0
- 弯曲模量 [MPa]: 7.20
- 硬度: 121.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.289 g/cc | 0.04657 lb/in³ | Melt; ISO 1183 | ||
| 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | |||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.7 % | 5.7 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | 0.2 in/min; ASTM Test | ||
| 51.0 MPa @Temperature 120 °C | 7400 psi @Temperature 248 °F | ISO Data | |||
| 51.0 MPa @Temperature 120 °C | 7400 psi @Temperature 248 °F | ASTM Test | |||
| 59.0 MPa @Temperature 80.0 °C | 8560 psi @Temperature 176 °F | ASTM Test | |||
| 59.0 MPa @Temperature 80.0 °C | 8560 psi @Temperature 176 °F | ISO Data | |||
| 178 MPa @Temperature -40.0 °C | 25800 psi @Temperature -40.0 °F | ASTM Test | |||
| 178 MPa @Temperature -40.0 °C | 25800 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ISO 527 | ||
| 2.0 % | 2.0 % | 0.2 in/min; ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ISO Data | |||
| 11 % @Temperature 120 °C | 11 % @Temperature 248 °F | ISO Data | |||
| 11 % @Temperature 120 °C | 11 % @Temperature 248 °F | ASTM Test | |||
| 13 % @Temperature 80.0 °C | 13 % @Temperature 176 °F | ASTM Test | |||
| 13 % @Temperature 80.0 °C | 13 % @Temperature 176 °F | ISO Data | |||
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1mm/min; ISO 527 | ||
| 2.62 GPa @Temperature 120 °C | 380 ksi @Temperature 248 °F | ISO Data | |||
| 3.09 GPa @Temperature 80.0 °C | 448 ksi @Temperature 176 °F | ISO Data | |||
| 10.79 GPa @Temperature -40.0 °C | 1565 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 178 MPa | 25800 psi | ISO Data | ||
| 200 MPa | 29000 psi | ASTM Test | |||
| Flexural Modulus | 7.20 GPa | 1040 ksi | ISO Data | ||
| 7.58 GPa | 1100 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.550 J/cm @Thickness 3.17 mm | 1.03 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO Test | ||
| 4.00 kJ/m² @Temperature -40.0 °C | 1.90 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | 4.60 J/cm² | 21.9 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 31.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 17.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Specific Heat Capacity | 2.028 J/g-°C | 0.4847 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| 202 °C | 396 °F | ASTM Test | |||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | BK-106 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| X | |||||
| X | |||||
| UL.UL-C | Yes | ||||