- 密度 [g/cm3]: 1.2784
- 吸水率 [%]: 0.9
- 缺口冲击强度: 1.34
- 弯曲强度 [MPa]: 215.0
- 弯曲模量 [MPa]: 11.4
- 硬度: 121.0
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.2784 g/cc | 0.046185 lb/in³ | Melt; ISO 1183 | ||
| 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | |||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.2 % | 5.2 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 230 MPa | 33400 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 215 MPa | 31200 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 0.2 in/min; ASTM Test | ||
| 3.0 % | 3.0 % | 5mm/min; ISO 527 | |||
| Tensile Modulus | 13.5 GPa | 1960 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 325 MPa | 47100 psi | ISO Data | ||
| 352 MPa | 51100 psi | ASTM Test | |||
| 138 MPa @Temperature 120 °C | 20000 psi @Temperature 248 °F | ASTM Test | |||
| 160 MPa @Temperature 93.0 °C | 23200 psi @Temperature 199 °F | ASTM Test | |||
| 220 MPa @Temperature 65.0 °C | 31900 psi @Temperature 149 °F | ASTM Test | |||
| 450 MPa @Temperature -40.0 °C | 65300 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 11.4 GPa | 1650 ksi | ISO Data | ||
| 11.7 GPa | 1700 ksi | ASTM Test | |||
| 4.83 GPa @Temperature 120 °C | 701 ksi @Temperature 248 °F | ASTM Test | |||
| 7.00 GPa @Temperature 65.0 °C | 1020 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 1.34 J/cm @Thickness 3.17 mm | 2.51 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO Test | ||
| 11.0 kJ/m² @Temperature -40.0 °C | 5.23 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 2.10 J/cm² | 9.99 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 31.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 17.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C | 17.8 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 79.0 µm/m-°C | 43.9 µin/in-°F | ISO 11359 | ||
| Specific Heat Capacity | 2.522 J/g-°C | 0.6028 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.329 W/m-K | 2.28 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 | ||
| 212 °C | 414 °F | ASTM Test | |||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||