BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned)

BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned) 物性表: BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned)物性表及特性介绍,BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned)注塑参数详情,如需BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned)下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.16
  • 吸水率 [%]: 0.9
  • 弯曲强度 [MPa]: 90.0
  • 弯曲模量 [MPa]: 4.83
 
Physical PropertiesMetricEnglishComments
Density 1.16 g/cc0.0419 lb/in³Melt; ISO 1183
 1.34 g/cc0.0484 lb/in³dry; ISO 1183
Water Absorption 0.90 %0.90 %24 hour; ISO Test
 5.5 %5.5 %beginning dry; ISO 62
Moisture Absorption at Equilibrium 1.5 %1.5 %beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage 0.0030 cm/cm0.0030 in/inASTM Data; MD
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 90.0 MPa13100 psi0.2 in/min; ASTM Test
Tensile Strength, Ultimate 90.0 MPa13100 psi5mm/min; ISO 527
Elongation at Break 6.0 %6.0 %5mm/min; ISO 527
 6.0 %6.0 %0.2 in/min; ASTM Test
Tensile Modulus 4.61 GPa669 ksi1mm/min; ISO 527
Flexural Strength 120 MPa17400 psiISO Data
 124 MPa18000 psiASTM Test
 90.0 MPa
@Temperature 120 °C
13100 psi
@Temperature 248 °F
ASTM Test
 100 MPa
@Temperature 93.0 °C
14500 psi
@Temperature 199 °F
ASTM Test
 110 MPa
@Temperature 65.0 °C
16000 psi
@Temperature 149 °F
ASTM Test
 297 MPa
@Temperature -40.0 °C
43100 psi
@Temperature -40.0 °F
ASTM Test
Flexural Modulus 4.83 GPa701 ksiASTM Test
 5.03 GPa730 ksiISO Data
 2.97 GPa
@Temperature 120 °C
431 ksi
@Temperature 248 °F
ASTM Test
 3.25 GPa
@Temperature 93.0 °C
471 ksi
@Temperature 199 °F
ASTM Test
 3.29 GPa
@Temperature 65.0 °C
477 ksi
@Temperature 149 °F
ASTM Test
 
Thermal PropertiesMetricEnglishComments
Specific Heat Capacity 1.958 J/g-°C0.4680 BTU/lb-°FMelt
Thermal Conductivity 0.200 W/m-K1.39 BTU-in/hr-ft²-°FMelt
Melting Point 220 °C428 °F10 K/min
 220 °C428 °FASTM Test
 
Processing PropertiesMetricEnglishComments
Melt Temperature 275 °C527 °FInjection molding
Mold Temperature 95.0 °C203 °FInjection molding
 
Descriptive Properties
ColorNatural
Commercial StatusActive America
FormPellets
Impact ModifiedYes
Primary Processing TechniqueInjection Molding
ProcessingInjection Molding
UL.UL-CYes

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-46109.html

免责声明: 本文 BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4