- 密度 [g/cm3]: 1.29
- 吸水率 [%]: 1.3
- 缺口冲击强度: 0.45
- 弯曲强度 [MPa]: 100.0
- 弯曲模量 [MPa]: 4.20
- 硬度: 119.0
- 热变形温度 [℃]: 211.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.3 % | 1.3 % | 24 hour; ISO Test | ||
| 7.9 % | 7.9 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM Test | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 5.20 GPa | 754 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 170 MPa | 24700 psi | ASTM Test | ||
| Flexural Modulus | 4.20 GPa | 609 ksi | ISO Data | ||
| 4.60 GPa | 667 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.450 J/cm @Thickness 3.17 mm | 0.843 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO Test | ||
| 3.00 kJ/m² @Temperature -40.0 °C | 1.43 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 | ||
| 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 211 °C | 412 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | ISO 75 | ||
| 193 °C | 379 °F | ASTM Test | |||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||