- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 1.1
- 缺口冲击强度: 1.55
- 拉伸强度 [MPa]: 32.0
- 弯曲模量 [MPa]: 0.620
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 6.7 % | 6.7 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 2 in/min; ASTM Test | ||
| 32.0 MPa | 4640 psi | 50mm/min; ISO 527 | |||
| 95.0 MPa @Temperature -40.0 °C | 13800 psi @Temperature -40.0 °F | ISO Data | |||
| 95.0 MPa @Temperature -40.0 °C | 13800 psi @Temperature -40.0 °F | ASTM Test | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |||
| Elongation at Yield | 9.0 % | 9.0 % | 50mm/min; ISO 527 | ||
| 9.0 % | 9.0 % | 2 in/min; ASTM Test | |||
| Tensile Modulus | 0.675 GPa | 97.9 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 30.0 MPa | 4350 psi | ASTM Test | ||
| 120 MPa @Temperature -40.0 °C | 17400 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 0.620 GPa | 89.9 ksi | ASTM Test | ||
| Izod Impact, Notched | 1.55 J/cm @Temperature -40.0 °C | 2.90 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| NB @Thickness 3.17 mm | NB @Thickness 0.125 in | ASTM Test | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 °C | 536 °F | Injection molding | ||
| Mold Temperature | 70.0 °C | 158 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Extrusion | ||||
| Processing | Injection Molding | ||||
| Other Extrusion | |||||
| Profile extrusion | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||