- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 1.1
- 拉伸强度 [MPa]: 52.0
- 弯曲模量 [MPa]: 1.60
- 硬度: 78.0
- 热变形温度 [℃]: 140.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| 6.7 % | 6.7 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 78 | 78 | ASTM Test | ||
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50mm/min; ISO 527 | ||
| 55.0 MPa | 7980 psi | 2 in/min; ASTM Test | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |||
| Elongation at Yield | 4.5 % | 4.5 % | 50mm/min; ISO 527 | ||
| 5.0 % | 5.0 % | 2 in/min; ASTM Test | |||
| Tensile Modulus | 1.80 GPa | 261 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 55.0 MPa | 7980 psi | ISO Data | ||
| 65.0 MPa | 9430 psi | ASTM Test | |||
| Flexural Modulus | 1.60 GPa | 232 ksi | ISO Data | ||
| 1.89 GPa | 274 ksi | ASTM Test | |||
| Izod Impact, Notched | NB @Thickness 3.17 mm | NB @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | NB | NB | ISO Test | ||
| 10.0 kJ/m² @Temperature -40.0 °C | 4.76 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 8.30 J/cm² | 39.5 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 106 µm/m-°C @Temperature -30.0 - 30.0 °C | 58.9 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 | ||
| 56.0 °C | 133 °F | ASTM Test | |||
| Flammability, UL94 | HB | HB | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 °C | 536 °F | Injection molding | ||
| Mold Temperature | 70.0 °C | 158 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Extrusion | ||||
| Processing | Injection Molding | ||||
| Other Extrusion | |||||
| Profile extrusion | |||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||