- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 9.5
- 缺口冲击强度: 40.0
- 拉伸强度 [MPa]: 73.0
- 弯曲模量 [MPa]: 2.23
- 硬度: 118.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Water Absorption | 9.5 % | 9.5 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.81 - 3.0 cP | 2.81 - 3.0 cP | ISO Test; 96 % SAV | ||
| Viscosity Test | 165 cm³/g | 165 cm³/g | Viscosity number | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM Test | ||
| Tensile Strength, Yield | 73.0 MPa | 10600 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 4.25 % | 4.25 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 2.50 GPa | 363 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 2.23 GPa | 323 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | ISO Test | ||
| 26.0 kJ/m² @Temperature -40.0 °C | 12.4 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Wire and Cable | ||||