- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 6.6
- 缺口冲击强度: 0.4
- 弯曲强度 [MPa]: 123.0
- 弯曲模量 [MPa]: 7.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.6 % | 6.6 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 123 MPa | 17800 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 123 MPa | 17800 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.6 % | 2.6 % | 0.2 in/min; ASTM Test | ||
| 2.7 % | 2.7 % | 5mm/min; ISO 527 | |||
| Tensile Modulus | 7.96 GPa | 1150 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 7.50 GPa | 1090 ksi | ISO Data | ||
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C | 0.749 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.530 J/cm @Thickness 3.17 mm | 0.993 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Izod Impact, Notched (ISO) | 4.80 kJ/m² | 2.28 ft-lb/in² | ISO Test | ||
| Charpy Impact, Notched | 0.410 J/cm² | 1.95 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | ASTM Test | ||
| 199 °C | 390 °F | ISO 75 | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||