- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 6.6
- 弯曲强度 [MPa]: 120.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.6 % | 6.6 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 130 cm³/g | 130 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD | ||
| Melt Flow | 25 g/10 min @Load 5.00 kg, Temperature 275 °C | 25 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179 | ||
| 5.00 J/cm² @Temperature -30.0 °C | 23.8 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 | ||
| 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz | 3.9 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 38.0 µm/m-°C | 21.1 µin/in-°F | ISO 11359 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 1.59 mm | HB @Thickness 0.0626 in | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||