- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 7.5
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 53.0
- 弯曲强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 4.48
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.5 % | 7.5 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 275 °C | 30 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 103 MPa | 14900 psi | 0.2 in/min; ASTM Test | ||
| 163 MPa @Temperature -40.0 °C | 23600 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5mm/min; ISO 527 | ||
| Tensile Strength, Yield | 53.0 MPa @Temperature 80.0 °C | 7690 psi @Temperature 176 °F | ISO Data | ||
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ISO 527 | ||
| 4.0 % | 4.0 % | 0.2 in/min; ASTM Test | |||
| 4.5 % @Temperature -40.0 °C | 4.5 % @Temperature -40.0 °F | ISO Data | |||
| Elongation at Yield | 8.6 % @Temperature 80.0 °C | 8.6 % @Temperature 176 °F | ISO Data | ||
| Tensile Modulus | 5.17 GPa | 750 ksi | ASTM Test | ||
| 5.50 GPa | 798 ksi | 1mm/min; ISO 527 | |||
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM Test | ||
| 4.50 GPa | 653 ksi | ISO Data | |||
| Izod Impact, Notched | 0.530 J/cm @Temperature -40.0 °C | 0.993 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 1.07 J/cm @Thickness 3.17 mm | 2.00 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179 | ||
| 5.50 J/cm² @Temperature -30.0 °C | 26.2 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179 | ||
| 0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.025 @Frequency 1.00e+6 Hz | 0.025 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.025 @Frequency 100 Hz | 0.025 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 33.0 µm/m-°C | 18.3 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ISO 11359 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 | ||
| 204 °C | 399 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 | ||
| 193 °C | 379 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 1.62 mm | HB @Thickness 0.0638 in | |||
| HB @Thickness 0.730 mm | HB @Thickness 0.0287 in | ||||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||