- 熔体流动速率 [g/10min]: 42.7
- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 7.2
- 缺口冲击强度: 15.0
- 拉伸强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 4.50
- 热变形温度 [℃]: 180.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.2 - 7.8 % | 7.2 - 7.8 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.1 - 2.7 % | 2.1 - 2.7 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Measurement | 160 | 160 | Viscosity Number; ISO 307 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |||
| Melt Flow | 42.7 g/10 min @Load 5.00 kg, Temperature 275 °C | 42.7 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 110 MPa | 16000 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 5.50 GPa | 798 ksi | ISO 527 | ||
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 | ||
| Flexural Modulus | 4.50 GPa | 653 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/A | ||
| 5.00 kJ/m² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 180/A | |||
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO 179/1eU | ||
| 5.50 J/cm² @Temperature -30.0 °C | 26.2 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179/1eA | ||
| 7.00 J/cm² @Temperature -30.0 °C | 33.3 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.025 @Frequency 1.00e+6 Hz | 0.025 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.300 - 0.350 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.167 - 0.194 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.700 - 0.800 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.389 - 0.444 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 180 °C | 356 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | BK30564 | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||