- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 1.0
- 缺口冲击强度: 1.5
- 弯曲强度 [MPa]: 185.0
- 弯曲模量 [MPa]: 9.67
- 硬度: 120.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.0 % | 1.0 % | 24 hour; ISO Test | ||
| 6.3 % | 6.3 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | ASTM Test | ||
| Tensile Strength at Break | 185 MPa | 26800 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 185 MPa | 26800 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527 | ||
| 3.5 % | 3.5 % | 0.2 in/min; ASTM Test | |||
| Flexural Strength | 290 MPa | 42100 psi | ASTM Test | ||
| Flexural Modulus | 9.67 GPa | 1400 ksi | ASTM Test | ||
| Izod Impact, Notched | 1.50 J/cm @Thickness 3.17 mm | 2.81 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||