- 熔体流动速率 [g/10min]: 72.6
- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 6.8
- 缺口冲击强度: 12.0
- 拉伸强度 [MPa]: 160.0
- 弯曲模量 [MPa]: 7.40
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.8 - 7.4 % | 6.8 - 7.4 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.1 - 2.5 % | 2.1 - 2.5 % | 23°C; 50% RH; ISO 62 | ||
| 2.3 % | 2.3 % | 50% RH | |||
| 7.1 % | 7.1 % | Saturation | |||
| Viscosity Measurement | 140 | 140 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | restricted | ||
| Melt Flow | 72.6 g/10 min @Load 5.00 kg, Temperature 275 °C | 72.6 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 30.0 MPa @Strain 1.00 %, Temperature 150 °C | 4350 psi @Strain 1.00 %, Temperature 302 °F | ISO 527 | ||
| 35.0 MPa @Strain 1.00 %, Temperature 120 °C | 5080 psi @Strain 1.00 %, Temperature 248 °F | ISO 527 | |||
| 38.0 MPa @Strain 1.00 %, Temperature 100 °C | 5510 psi @Strain 1.00 %, Temperature 212 °F | ISO 527 | |||
| 45.0 MPa @Strain 2.00 %, Temperature 150 °C | 6530 psi @Strain 2.00 %, Temperature 302 °F | ISO 527 | |||
| 60.0 MPa @Strain 2.00 %, Temperature 120 °C | 8700 psi @Strain 2.00 %, Temperature 248 °F | ISO 527 | |||
| 65.0 MPa @Strain 2.00 %, Temperature 100 °C | 9430 psi @Strain 2.00 %, Temperature 212 °F | ISO 527 | |||
| 70.0 MPa @Strain 1.00 %, Temperature 60.0 °C | 10200 psi @Strain 1.00 %, Temperature 140 °F | ISO 527 | |||
| 83.0 MPa @Strain 1.00 %, Temperature 23.0 °C | 12000 psi @Strain 1.00 %, Temperature 73.4 °F | ISO 527 | |||
| 100 MPa @Strain 1.00 %, Temperature -20.0 °C | 14500 psi @Strain 1.00 %, Temperature -4.00 °F | ISO 527 | |||
| 100 MPa @Strain 2.00 %, Temperature 60.0 °C | 14500 psi @Strain 2.00 %, Temperature 140 °F | ISO 527 | |||
| 143 MPa @Strain 2.00 %, Temperature 23.0 °C | 20700 psi @Strain 2.00 %, Temperature 73.4 °F | ISO 527 | |||
| 170 MPa @Strain 2.00 %, Temperature -20.0 °C | 24700 psi @Strain 2.00 %, Temperature -4.00 °F | ISO 527 | |||
| Tensile Strength, Yield | 160 MPa | 23200 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 8.00 GPa | 1160 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 220 MPa | 31900 psi | at max force; ISO 178 | ||
| Flexural Modulus | 7.40 GPa | 1070 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature -30.0 °C | 35.7 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 8.00 J/cm² @Temperature 23.0 °C | 38.1 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00 Hz | 3.8 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.025 @Frequency 1.00e+6 Hz | 0.025 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 450 V | 450 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.200 - 0.250 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.111 - 0.139 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.600 - 0.700 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.333 - 0.389 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |||
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr | ||
| 175 °C | 347 °F | for 50% loss of tensile strength after 5000hr | |||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| UL RTI, Electrical | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical with Impact | 95.0 °C @Thickness 1.50 mm | 203 °F @Thickness 0.0591 in | 764B | ||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | 764B | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 260 °C | 500 °F | Feed Zone | ||
| Zone 2 | 270 °C | 518 °F | Compression | ||
| Zone 3 | 280 °C | 536 °F | Metering-zone | ||
| Zone 4 | 280 °C | 536 °F | Nozzle | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion | ||
| 280 °C | 536 °F | Optimal | |||
| Mold Temperature | 80.0 °C | 176 °F | Optimal | ||
| 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D129 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||