- 熔体流动速率 [g/10min]: 116.45
- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 6.9
- 拉伸强度 [MPa]: 115.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.9 - 7.5 % | 6.9 - 7.5 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.1 - 2.5 % | 2.1 - 2.5 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 123 | 123 | ISO 307 | ||
| Melt Flow | 116.45 g/10 min @Load 5.00 kg, Temperature 275 °C | 116.45 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 3.60 GPa | 522 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 6.2 @Frequency 1.00 Hz | 6.2 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz | 0.20 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 180 °C | 356 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | BK 23210 | ||||
| Commercial Status | Europe | ||||