- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 4.3
- 拉伸强度 [MPa]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.3 - 5.3 % | 4.3 - 5.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.80 - 1.2 % | 0.80 - 1.2 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0033 cm/cm | 0.0033 in/in | restricted | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 40.0 MPa @Strain 2.00 %, Temperature 150 °C | 5800 psi @Strain 2.00 %, Temperature 302 °F | 5mm/min | ||
| 50.0 MPa @Strain 2.00 %, Temperature 100 °C | 7250 psi @Strain 2.00 %, Temperature 212 °F | 5mm/min | |||
| 60.0 MPa @Strain 6.00 %, Temperature 150 °C | 8700 psi @Strain 6.00 %, Temperature 302 °F | 5mm/min | |||
| 65.0 MPa @Strain 9.00 %, Temperature 150 °C | 9430 psi @Strain 9.00 %, Temperature 302 °F | 5mm/min | |||
| 75.0 MPa @Strain 6.00 %, Temperature 100 °C | 10900 psi @Strain 6.00 %, Temperature 212 °F | 5mm/min | |||
| 80.0 MPa @Strain 9.00 %, Temperature 100 °C | 11600 psi @Strain 9.00 %, Temperature 212 °F | 5mm/min | |||
| 100 MPa @Strain 2.00 %, Temperature 80.0 °C | 14500 psi @Strain 2.00 %, Temperature 176 °F | 5mm/min | |||
| 110 MPa @Strain 1.00 %, Temperature 60.0 °C | 16000 psi @Strain 1.00 %, Temperature 140 °F | 5mm/min | |||
| 120 MPa @Strain 3.00 %, Temperature 80.0 °C | 17400 psi @Strain 3.00 %, Temperature 176 °F | 5mm/min | |||
| 125 MPa @Strain 5.00 %, Temperature 80.0 °C | 18100 psi @Strain 5.00 %, Temperature 176 °F | 5mm/min | |||
| 160 MPa @Strain 2.00 %, Temperature 60.0 °C | 23200 psi @Strain 2.00 %, Temperature 140 °F | 5mm/min | |||
| 175 MPa @Strain 1.00 %, Temperature 23.0 °C | 25400 psi @Strain 1.00 %, Temperature 73.4 °F | 5mm/min | |||
| 200 MPa @Strain 2.00 %, Temperature 23.0 °C | 29000 psi @Strain 2.00 %, Temperature 73.4 °F | 5mm/min | |||
| Tensile Strength, Yield | 210 MPa | 30500 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | ISO 527-1/-2 | ||
| 5.00 GPa @Temperature 140 °C | 725 ksi @Temperature 284 °F | ISO 527 | |||
| 9.00 GPa @Temperature 80.0 °C | 1310 ksi @Temperature 176 °F | ISO 527 | |||
| 12.0 GPa @Temperature 0.000 °C | 1740 ksi @Temperature 32.0 °F | ISO 527 | |||
| 12.0 GPa @Temperature 40.0 °C | 1740 ksi @Temperature 104 °F | ISO 527 | |||
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature 23.0 °C | 47.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.70 J/cm² @Temperature 23.0 °C | 8.09 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| 2.00e+9 ohm-cm @Temperature 140 °C | 2.00e+9 ohm-cm @Temperature 284 °F | IEC 60093 | |||
| 6.00e+10 ohm-cm @Temperature 120 °C | 6.00e+10 ohm-cm @Temperature 248 °F | IEC 60093 | |||
| 1.00e+13 ohm-cm @Temperature 100 °C | 1.00e+13 ohm-cm @Temperature 212 °F | IEC 60093 | |||
| 1.00e+15 ohm-cm @Temperature 80.0 °C | 1.00e+15 ohm-cm @Temperature 176 °F | IEC 60093 | |||
| 5.00e+15 ohm-cm @Temperature 60.0 °C | 5.00e+15 ohm-cm @Temperature 140 °F | IEC 60093 | |||
| 5.00e+15 ohm-cm @Temperature 20.0 °C | 5.00e+15 ohm-cm @Temperature 68.0 °F | IEC 60093 | |||
| 1.00e+16 ohm-cm @Temperature 40.0 °C | 1.00e+16 ohm-cm @Temperature 104 °F | IEC 60093 | |||
| Dielectric Constant | 4.2 @Frequency 1.00 Hz | 4.2 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.500 - 0.600 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.278 - 0.333 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.150 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.0833 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |||
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr | ||
| 160 °C | 320 °F | for 50% loss of tensile strength after 5000hr | |||
| 270 °C | 518 °F | ||||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||