- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 4.3
- 拉伸强度 [MPa]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.3 - 5.3 % | 4.3 - 5.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.80 - 1.2 % | 0.80 - 1.2 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0033 cm/cm | 0.0033 in/in | restricted | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 200 MPa | 29000 psi | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | ISO 527-1/-2 | ||
| Tensile Creep Modulus, 1000 hours | 8700 MPa @Strain <=0.500 % | 1.26e+6 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 | ||
| 1.00e+8 ohm-cm @Temperature 140 °C | 1.00e+8 ohm-cm @Temperature 284 °F | IEC 60093 | |||
| 2.00e+10 ohm-cm @Temperature 100 °C | 2.00e+10 ohm-cm @Temperature 212 °F | IEC 60093 | |||
| 1.00e+11 ohm-cm @Temperature 80.0 °C | 1.00e+11 ohm-cm @Temperature 176 °F | IEC 60093 | |||
| 5.00e+11 ohm-cm @Temperature 60.0 °C | 5.00e+11 ohm-cm @Temperature 140 °F | IEC 60093 | |||
| 1.00e+13 ohm-cm @Temperature 40.0 °C | 1.00e+13 ohm-cm @Temperature 104 °F | IEC 60093 | |||
| 1.00e+15 ohm-cm @Temperature 20.0 °C | 1.00e+15 ohm-cm @Temperature 68.0 °F | IEC 60093 | |||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 4.4 @Frequency 1.00 Hz | 4.4 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.030 @Frequency 1.00e+6 Hz | 0.030 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |||
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr | ||
| 160 °C | 320 °F | for 50% loss of tensile strength after 5000hr | |||
| 270 °C | 518 °F | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||