- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 5.0
- 拉伸强度 [MPa]: 140.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.0 - 6.0 % | 5.0 - 6.0 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.1 - 1.5 % | 1.1 - 1.5 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | restricted | ||
| Linear Mold Shrinkage, Flow | 0.0041 cm/cm | 0.0041 in/in | TM=320°C, TW=100°C | ||
| 0.0050 cm/cm | 0.0050 in/in | ISO 2577 | |||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 140 MPa | 20300 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 8.00 GPa | 1160 ksi | ISO 527-1/-2 | ||
| Tensile Creep Modulus, 1000 hours | 6400 MPa @Strain <=0.500 % | 928000 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.310 W/m-K | 2.15 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 125 °C | 257 °F | for 50% loss of tensile strength after 20000hr | ||
| 150 °C | 302 °F | for 50% loss of tensile strength after 5000hr | |||
| 270 °C | 518 °F | ||||
| Decomposition Temperature | >= 350 °C | >= 662 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 300 °C | 572 °F | Feed Zone | ||
| Zone 2 | 310 °C | 590 °F | Compression | ||
| Zone 3 | 320 °C | 608 °F | Metering-zone | ||
| Zone 4 | 320 °C | 608 °F | Nozzle | ||
| Melt Temperature | >= 320 °C | >= 608 °F | Optimal | ||
| 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion | |||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Injection-molding | ||
| 100 °C | 212 °F | Optimal | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 8 hour | 8 hour | |||
| Descriptive Properties | |||||
| Color | BK 00100 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >470°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||