- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 6.5
- 拉伸强度 [MPa]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.5 - 7.5 % | 6.5 - 7.5 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.6 - 2.0 % | 1.6 - 2.0 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | restricted | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 3.20 GPa | 464 ksi | ISO 527-1/-2 | ||
| Tensile Creep Modulus, 1000 hours | 2300 MPa @Strain <=0.500 % | 334000 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 1.00 Hz | 4.0 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.040 @Frequency 1.00e+6 Hz | 0.040 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |||
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 110 °C | 230 °F | for 50% loss of tensile strength after 20000hr | ||
| 130 °C | 266 °F | for 50% loss of tensile strength after 5000hr | |||
| 250 °C | 482 °F | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||