- 密度 [g/cm3]: 1.52
- 拉伸强度 [MPa]: 48.0
- 热变形温度 [℃]: 265.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.80 - 1.2 % | 0.80 - 1.2 % | 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | 5mm/min; ISO 527-2 | ||
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ISO 527 | ||
| Elongation at Break | 2.1 % | 2.1 % | ISO 527-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 | ||
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 4.00e+12 ohm-cm | 4.00e+12 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ISO 60093 | ||
| Dielectric Constant | 4.4 @Frequency 1.00e+6 Hz | 4.4 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.300 µm/m-°C | 0.167 µin/in-°F | DIN 53152 | ||
| CTE, linear, Transverse to Flow | 0.500 µm/m-°C | 0.278 µin/in-°F | DIN 53752 | ||
| Melting Point | 295 °C | 563 °F | ISO 3146 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | ISO 75-2 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Commercial Status | Europe | ||||