- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 4.0
- 缺口冲击强度: 23.0
- 拉伸强度 [MPa]: 165.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.0 - 5.0 % | 4.0 - 5.0 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.60 - 1.0 % | 0.60 - 1.0 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | restricted | ||
| Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | TM=320°C, TW=100°C | ||
| 0.0040 cm/cm | 0.0040 in/in | ISO 2577 | |||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 165 MPa | 23900 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 9.30 GPa | 1350 ksi | ISO 527-1/-2 | ||
| Izod Impact, Notched (ISO) | 23.0 kJ/m² @Temperature 23.0 °C | 10.9 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 9.50 J/cm² @Temperature 23.0 °C | 45.2 ft-lb/in² @Temperature 73.4 °F | ISO 179 | ||
| Charpy Impact, Notched | 1.90 J/cm² @Temperature 23.0 °C | 9.04 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 4.3 @Frequency 1.00 Hz | 4.3 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.030 @Frequency 1.00e+6 Hz | 0.030 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.500 - 0.600 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.278 - 0.333 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.250 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.139 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 130 °C | 266 °F | for 50% loss of tensile strength after 20000hr | ||
| 160 °C | 320 °F | for 50% loss of tensile strength after 5000hr | |||
| 270 °C | 518 °F | ||||
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 350 °C | >= 662 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 300 °C | 572 °F | Feed Zone | ||
| Zone 2 | 310 °C | 590 °F | Compression | ||
| Zone 3 | 320 °C | 608 °F | Metering-zone | ||
| Zone 4 | 320 °C | 608 °F | Nozzle | ||
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion | ||
| 320 °C | 608 °F | Optimal | |||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Injection-molding | ||
| 100 °C | 212 °F | Optimal | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 8 hour | 8 hour | |||
| Moisture Content | <= 0.030 % | <= 0.030 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Color | BK 00564 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >470°C | ASTM D1929 | |||
| Peripheral Screw Speed | <0.3 m/s | ||||