- 密度 [g/cm3]: 1.07
- 拉伸强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 1.655
- 硬度: 78.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 | ||
Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 24 Hours; ASTM D570 | ||
1.9 % | 1.9 % | 50% RH; ASTM D570 | |||
6.7 % | 6.7 % | Saturation; ASTM D570 | |||
Linear Mold Shrinkage | 0.03556 cm/cm | 0.03556 in/in | 1/8" bar | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Rockwell R | 78 | 78 | ASTM D785 | ||
Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM D638 | ||
Elongation at Break | >= 100 % | >= 100 % | ASTM D638 | ||
Flexural Strength | 66.0 MPa | 9570 psi | ASTM D790 | ||
Flexural Modulus | 1.655 GPa | 240.0 ksi | ASTM D 790 | ||
Izod Impact, Notched (ISO) | NB | NB | ASTM D256 | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear | 1.06 µm/m-°C | 0.589 µin/in-°F | ASTM E831 | ||
Melting Point | 220 °C | 428 °F | ASTM D3418 | ||
Processing Properties | Metric | English | Comments | ||
Melt Temperature | 240 - 270 °C | 464 - 518 °F | |||
Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |||
Dry Time | 2 - 4 hour | 2 - 4 hour | |||
Moisture Content | <= 0.20 % | <= 0.20 % | |||
Descriptive Properties | |||||
Color | BK 106 | ||||
Commercial Status | North America |