- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.5
- 缺口冲击强度: 0.9
- 断裂伸长率 [%]: 109
- 弯曲强度 [MPa]: 74.0
- 弯曲模量 [MPa]: 3.10
- 硬度: 112.0
- 热变形温度 [℃]: 204.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 2.5 % | 2.5 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Ultimate | 74.0 MPa | 10700 psi | ASTM D638 |
| Elongation at Break | 35 - 45 % | 35 - 45 % | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Yield Strength | 109 MPa | 15800 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Compressive Yield Strength | 95.0 MPa | 13800 psi | 10% Offset; ASTM D695 |
| Compressive Modulus | 2.40 GPa | 348 ksi | ASTM D695 |
| Shear Strength | 59.0 MPa | 8560 psi | ASTM D732 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Tensile Impact Strength | 72.0 kJ/m² | 34.3 ft-lb/in² | ASTM D1822 |
| Coefficient of Friction, Dynamic | 0.12 | 0.12 | |
| Coefficient of Friction, Static | 0.20 | 0.20 | |
| K (wear) Factor | 8.06 x 10-8 mm³/N-M | 4.00 x 10-10 in³-min/ft-lb-hr | unlubricated thrust washer machine @ 10 fpm and 250 psi |
| Limiting Pressure Velocity | 0.560 MPa-m/sec | 16000 psi-ft/min | at 1.27 m/s |
| 1.33 MPa-m/sec | 38000 psi-ft/min | at 0.127 m/s | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 63.0 µm/m-°C @Temperature 20.0 °C | 35.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 226 - 238 °C | 439 - 460 °F | ASTM D789 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous service |
| 166 °C | 331 °F | Intermittent service | |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 - 221 °C | 399 - 430 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 - 204 °C | 331 - 399 °F | ASTM D648 |