- 密度 [g/cm3]: 1.13
- 缺口冲击强度: 5.5
- 拉伸强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 2.62
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 24 Hours | ||
| 2.7 % | 2.7 % | 50% RH | |||
| 9.5 % | 9.5 % | Saturation | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 | ||
| Elongation at Break | 44 % | 44 % | Nominal; ISO 527 | ||
| Flexural Modulus | 2.62 GPa | 380 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO 180 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ISO 75 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 285 °C | 464 - 545 °F | |||
| Mold Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | 0.15 % | 0.15 % | |||
| Descriptive Properties | |||||
| Color | BK 6 | ||||
| Commercial Status | North America | ||||