- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.5
- 缺口冲击强度: 0.4
- 断裂伸长率 [%]: 107
- 弯曲强度 [MPa]: 88.0
- 弯曲模量 [MPa]: 3.00
- 硬度: 112.0
- 热变形温度 [℃]: 204.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 5.5 % | 5.5 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Hardness, Shore D | 77 | 77 | ASTM D2240 |
| Tensile Strength, Ultimate | 88.0 MPa | 12800 psi | ASTM D638 |
| Elongation at Break | 20 - 30 % | 20 - 30 % | ASTM D638 |
| Tensile Modulus | 2.90 GPa | 421 ksi | ASTM D638 |
| Flexural Yield Strength | 107 MPa | 15500 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Compressive Modulus | 2.10 GPa | 305 ksi | ASTM D695 |
| Shear Strength | 72.0 MPa | 10400 psi | ASTM D732 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 81.0 µm/m-°C @Temperature 20.0 °C | 45.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 226 - 238 °C | 439 - 460 °F | ASTM D789 |
| Maximum Service Temperature, Air | 121 °C | 250 °F | Continuous service |
| 166 °C | 331 °F | Intermittent service | |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 - 221 °C | 399 - 430 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 - 204 °C | 331 - 399 °F | ASTM D648 |