- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.9
- 缺口冲击强度: 0.534
- 弯曲模量 [MPa]: 7.58
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Filler Content | 40 % | 40 % | |
| Water Absorption | 0.90 % | 0.90 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 0.125 in; ASTM D256 |
| Tensile Impact Strength | 147 kJ/m² | 70.0 ft-lb/in² | Type S; ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 216 - 220 °C | 420 - 428 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Unannealed; ASTM D648 |