- 缺口冲击强度: 1.87
- 拉伸强度 [MPa]: 57.2
- 断裂伸长率 [%]: 103
- 弯曲模量 [MPa]: 2.55
- 热变形温度 [℃]: 82.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 57.2 MPa | 8300 psi | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm @Temperature 22.8 °C | 3.50 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | |
| Mold Temperature | 51.7 - 79.4 °C | 125 - 175 °F | |
| Dry Time | 2 - 4 hour @Temperature 104 °C | 2 - 4 hour @Temperature 220 °F | to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |