- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.05
- 弯曲模量 [MPa]: 5.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ISO 2577 |
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 240 °C | 15 g/10 min @Load 22.0 lb, Temperature 464 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 6.50 GPa | 943 ksi | ISO 527 |
| Flexural Modulus | 5.80 GPa | 841 ksi | ISO 178 |
| Izod Impact, Notched | 0.0500 J/cm @Temperature 23.0 °C | 0.0937 ft-lb/in @Temperature 73.4 °F | ISO 180/A |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 135 °C @Load 0.999 kg | 275 °F @Load 2.20 lb | 50°C/hr; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||