- 熔体流动速率 [g/10min]: 27.0
- 密度 [g/cm3]: 1.12
- 缺口冲击强度: 0.06
- 弯曲模量 [MPa]: 3.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 2577 |
| Melt Flow | 27 g/10 min @Load 10.0 kg, Temperature 240 °C | 27 g/10 min @Load 22.0 lb, Temperature 464 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 3.70 GPa | 537 ksi | ISO 527 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| Izod Impact, Notched | 0.0600 J/cm @Temperature 23.0 °C | 0.112 ft-lb/in @Temperature 73.4 °F | ISO 180/A |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 115 °C @Load 5.00 kg | 239 °F @Load 11.0 lb | 50°C/hr; ISO 306 |
| 190 °C @Load 0.999 kg | 374 °F @Load 2.20 lb | 50°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | |
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||