- 吸水率 [%]: 1.3
- 缺口冲击强度: 2.14
- 拉伸强度 [MPa]: 35.9
- 弯曲模量 [MPa]: 0.827
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | 24 hours Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.011 - 0.015 cm/cm | 0.011 - 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
| Elongation at Break | 250 % | 250 % | ASTM D638 |
| Flexural Strength | 43.4 MPa | 6300 psi | ASTM D790 |
| Flexural Modulus | 0.827 GPa | 120 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm | 4.00 ft-lb/in | 1/8 in specimen; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 218 °C | 424 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.3 °C | 110 °F | 0.125 in bar; ASTM D648 |