- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 7.0
- 热变形温度 [℃]: 190.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | Humidity Absorption; Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527-1/-2 | ||
| Elongation at Break | 15 % | 15 % | ISO 527-1/-2 | ||
| Tensile Modulus | 5.00 GPa | 725 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 12.0 J/cm² @Temperature -30.0 °C | 57.1 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 19.0 J/cm² @Temperature 23.0 °C | 90.4 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.550 J/cm² @Temperature -30.0 °C | 2.62 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.800 J/cm² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Release Agent | Yes | ||||
| With Fillers | Yes | ||||