- 密度 [g/cm3]: 1.1
- 缺口冲击强度: 10.0
- 弯曲强度 [MPa]: 58.0
- 弯曲模量 [MPa]: 2.485
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 79 | 79 | ISO 868 |
| Tensile Strength, Ultimate | 58.0 MPa | 8410 psi | ISO 527 |
| Elongation at Break | 40 % | 40 % | ISO 527 |
| Modulus of Elasticity | 2.445 GPa | 354.6 ksi | ISO 527 |
| Flexural Modulus | 2.485 GPa | 360.4 ksi | ISO 178 |
| Shear Modulus | 1.00 GPa | 145 ksi | torsional |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180, Brittle break |
| 7.00 kJ/m² @Temperature -40.0 °C | 3.33 ft-lb/in² @Temperature -40.0 °F | Brittle break; ISO 180 | |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | DIN 53453, Brittle break |
| 0.600 J/cm² @Temperature -40.0 °C | 2.86 ft-lb/in² @Temperature -40.0 °F | Brittle break; DIN 53453 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 214 °C | 417 °F | DSC |