- 密度 [g/cm3]: 1.05
- 缺口冲击强度: 13.0
- 弯曲模量 [MPa]: 0.850
- 热变形温度 [℃]: 85.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 44.0 MPa @Temperature 23.0 °C | 6380 psi @Temperature 73.4 °F | DAM; 50mm/min; ISO 527 | ||
| Elongation at Break | 200 % @Temperature 23.0 °C | 200 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 230 % @Temperature 23.0 °C | 230 % @Temperature 73.4 °F | DAM; 50mm/min; ISO 527 | |||
| Tensile Modulus | 0.850 GPa @Temperature 23.0 °C | 123 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 0.850 GPa @Temperature 23.0 °C | 123 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature -40.0 °C | 6.19 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 36.0 kJ/m² @Temperature -20.0 °C | 17.1 ft-lb/in² @Temperature -4.00 °F | DAM; ISO 180/1A | |||
| 65.0 kJ/m² @Temperature 23.0 °C | 30.9 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 180/1U | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -40.0 °C | 5.71 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 8.00 J/cm² @Temperature 23.0 °C | 38.1 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 130 µm/m-°C @Temperature 23.0 - 55.0 °C | 72.2 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 140 µm/m-°C @Temperature 23.0 - 55.0 °C | 77.8 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Melting Point | 218 °C | 424 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 °C | 104 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 °C | 464 °F | DAM; optimum; Extrusion | ||
| 235 - 250 °C | 455 - 482 °F | DAM; Extrusion | |||
| 270 °C | 518 °F | DAM; optimum; Injection Molding | |||
| 260 - 280 °C | 500 - 536 °F | DAM; Injection Molding | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; Optimum; Injection Molding | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Injection Molding | ||
| 80.0 °C | 176 °F | DAM; Extrusion | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Dehumidified Dryer; Injection Molding | ||
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Dehumidified Dryer; Extrusion | |||
| Moisture Content | <= 0.060 % | <= 0.060 % | DAM; Extrusion | ||
| <= 0.060 % | <= 0.060 % | DAM; Injection Molding | |||
| Descriptive Properties | |||||
| Additive | Carbon Black | ||||
| Heat Stabilizer | |||||
| Impact Modifier, Rubber | |||||
| Appearance | Natural Color | ||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | ||||
| Features | Elongation, Good | ||||
| Flexibility, Good | |||||
| Heat Aging Resistance, Good | |||||
| Heat Stabilized | |||||
| Impact Modified | |||||
| Impact Resistance, Good | |||||
| Lubricated | |||||
| Toughness, Good | |||||
| Forms | Pellets | ||||
| Generic | Nylon 6 | ||||
| Material Status | Current | ||||
| Part Marking Code | >PA6-HI< | ISO 11469 | |||
| Processing Method | Extrusion | ||||
| Product Category | Extrusion Resins | ||||
| Toughened Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PA6-HI | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Cable Jacketing | ||||
| Liners | |||||