- 吸水率 [%]: 2.5
- 缺口冲击强度: 6.03
- 弯曲强度 [MPa]: 44.0
- 弯曲模量 [MPa]: 1.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 2.5 % | 2.5 % | 24 hrs; DIN 53714 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 73 | 73 | |
| Tensile Strength, Ultimate | 44.0 MPa | 6380 psi | ASTM D638 |
| Elongation at Break | 320 % | 320 % | ASTM D638 |
| Tensile Modulus | 0.900 GPa | 131 ksi | ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Izod Impact, Notched | 6.03 J/cm | 11.3 ft-lb/in | Method B; Ductile Failure |
| 1.01 J/cm @Temperature -40.0 °C | 1.89 ft-lb/in @Temperature -40.0 °F | Method B; Brittle Failure | |
| Charpy Impact, Notched | 1.65 J/cm² | 7.85 ft-lb/in² | Ductile Failure; ASTM D256B |
| 0.600 J/cm² @Temperature -40.0 °C | 2.86 ft-lb/in² @Temperature -40.0 °F | Method B; Brittle Failure | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.2 @Frequency 100000 Hz | 4.2 @Frequency 100000 Hz | |
| 7.8 @Frequency 1000 Hz | 7.8 @Frequency 1000 Hz | ||
| 14.9 @Frequency 50 Hz | 14.9 @Frequency 50 Hz | ||
| Dielectric Strength | 13.0 kV/mm | 330 kV/in | |
| Dissipation Factor | 0.10 @Frequency 100000 Hz | 0.10 @Frequency 100000 Hz | ASTM D150 |
| 0.30 @Frequency 1000 Hz | 0.30 @Frequency 1000 Hz | ASTM D150 | |
| Comparative Tracking Index | 500 V | 500 V | ASTM D257 |