  3. PA6
  4. DuPont Performance Polymers Zytel® PLUS PLS93G35DH1 BK261 Nylon 6

DuPont Performance Polymers Zytel® PLUS PLS93G35DH1 BK261 Nylon 6

DuPont Performance Polymers Zytel® PLUS PLS93G35DH1 BK261 Nylon 6 物性表: DuPont Performance Polymers Zytel® PLUS PLS93G35DH1 BK261 Nylon 6物性表及特性介绍,DuPont Performance Polymers Zytel® PLUS PLS93G35DH1 BK261 Nylon 6注塑参数详情,如需DuPont Performance Polymers Zytel® PLUS PLS93G35DH1 BK261 Nylon 6下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.4
  • 吸水率 [%]: 2.0
  • 弯曲模量 [MPa]: 10.1
  • 热变形温度 [℃]: 220.0
 
Physical PropertiesMetricEnglishComments
Density 1.40 g/cc0.0506 lb/in³DAM; ISO 1183
Filler Content 35 %35 %DAM
Water Absorption 2.0 %
@Temperature 23.0 °C		2.0 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0020 cm/cm
@Thickness 2.00 mm		0.0020 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  120 MPa
@Temperature 23.0 °C		17400 psi
@Temperature 73.4 °F		50%RH; ISO 527
 197 MPa
@Temperature 23.0 °C		28600 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Stress  0.510 MPa
@Strain 0.000 %,
Temperature 200 °C		74.0 psi
@Strain 0.000 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 0.830 MPa
@Strain 0.000 %,
Temperature 180 °C		120 psi
@Strain 0.000 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 0.880 MPa
@Strain 0.000 %,
Temperature 150 °C		128 psi
@Strain 0.000 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.910 MPa
@Strain 0.000 %,
Temperature 150 °C		132 psi
@Strain 0.000 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.950 MPa
@Strain 0.000 %,
Temperature 120 °C		138 psi
@Strain 0.000 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 1.09 MPa
@Strain 0.000 %,
Temperature 120 °C		158 psi
@Strain 0.000 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 1.09 MPa
@Strain 0.000 %,
Temperature 90.0 °C		158 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 1.17 MPa
@Strain 0.000 %,
Temperature 90.0 °C		170 psi
@Strain 0.000 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 1.19 MPa
@Strain 0.000 %,
Temperature 60.0 °C		173 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 1.23 MPa
@Strain 0.000 %,
Temperature 40.0 °C		178 psi
@Strain 0.000 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 1.28 MPa
@Strain 0.000 %,
Temperature 23.0 °C		186 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 1.34 MPa
@Strain 0.000 %,
Temperature 0.000 °C		194 psi
@Strain 0.000 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 1.38 MPa
@Strain 0.000 %,
Temperature 60.0 °C		200 psi
@Strain 0.000 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 1.56 MPa
@Strain 0.000 %,
Temperature 0.000 °C		226 psi
@Strain 0.000 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 1.81 MPa
@Strain 0.000 %,
Temperature 40.0 °C		263 psi
@Strain 0.000 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 1.92 MPa
@Strain 0.000 %,
Temperature -20.0 °C		278 psi
@Strain 0.000 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 1.95 MPa
@Strain 0.000 %,
Temperature -20.0 °C		283 psi
@Strain 0.000 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 1.98 MPa
@Strain 0.000 %,
Temperature 23.0 °C		287 psi
@Strain 0.000 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 2.76 MPa
@Strain 0.0400 %,
Temperature -20.0 °C		400 psi
@Strain 0.0400 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 2.90 MPa
@Strain 0.100 %,
Temperature 200 °C		421 psi
@Strain 0.100 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 2.94 MPa
@Strain 0.0600 %,
Temperature 150 °C		426 psi
@Strain 0.0600 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.19 MPa
@Strain 0.0600 %,
Temperature 180 °C		463 psi
@Strain 0.0600 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 3.32 MPa
@Strain 0.0600 %,
Temperature 120 °C		482 psi
@Strain 0.0600 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 3.75 MPa
@Strain 0.0200 %,
Temperature -20.0 °C		544 psi
@Strain 0.0200 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 3.90 MPa
@Strain 0.0700 %,
Temperature 150 °C		566 psi
@Strain 0.0700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 3.92 MPa
@Strain 0.0500 %,
Temperature 90.0 °C		569 psi
@Strain 0.0500 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 4.40 MPa
@Strain 0.0600 %,
Temperature 60.0 °C		638 psi
@Strain 0.0600 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 4.42 MPa
@Strain 0.0700 %,
Temperature 120 °C		641 psi
@Strain 0.0700 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 4.70 MPa
@Strain 0.0600 %,
Temperature 40.0 °C		682 psi
@Strain 0.0600 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 4.86 MPa
@Strain 0.0800 %,
Temperature 90.0 °C		705 psi
@Strain 0.0800 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 4.88 MPa
@Strain 0.190 %,
Temperature 200 °C		708 psi
@Strain 0.190 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 4.95 MPa
@Strain 0.110 %,
Temperature 150 °C		718 psi
@Strain 0.110 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.23 MPa
@Strain 0.0500 %,
Temperature 23.0 °C		759 psi
@Strain 0.0500 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 5.52 MPa
@Strain 0.0700 %,
Temperature 60.0 °C		801 psi
@Strain 0.0700 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 5.54 MPa
@Strain 0.140 %,
Temperature 180 °C		804 psi
@Strain 0.140 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 5.69 MPa
@Strain 0.0500 %,
Temperature 0.000 °C		825 psi
@Strain 0.0500 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 5.70 MPa
@Strain 0.120 %,
Temperature 120 °C		827 psi
@Strain 0.120 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 5.99 MPa
@Strain 0.0500 %,
Temperature 40.0 °C		869 psi
@Strain 0.0500 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 6.51 MPa
@Strain 0.0400 %,
Temperature 23.0 °C		944 psi
@Strain 0.0400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 6.60 MPa
@Strain 0.120 %,
Temperature 90.0 °C		957 psi
@Strain 0.120 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 6.76 MPa
@Strain 0.0500 %,
Temperature 0.000 °C		980 psi
@Strain 0.0500 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 6.90 MPa
@Strain 0.170 %,
Temperature 150 °C		1000 psi
@Strain 0.170 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.94 MPa
@Strain 0.150 %,
Temperature 150 °C		1010 psi
@Strain 0.150 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.54 MPa
@Strain 0.0900 %,
Temperature -20.0 °C		1090 psi
@Strain 0.0900 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 7.63 MPa
@Strain 0.110 %,
Temperature 60.0 °C		1110 psi
@Strain 0.110 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 7.69 MPa
@Strain 0.200 %,
Temperature 180 °C		1120 psi
@Strain 0.200 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 7.75 MPa
@Strain 0.150 %,
Temperature 120 °C		1120 psi
@Strain 0.150 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 7.91 MPa
@Strain 0.180 %,
Temperature 120 °C		1150 psi
@Strain 0.180 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.13 MPa
@Strain 0.110 %,
Temperature 40.0 °C		1180 psi
@Strain 0.110 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 8.56 MPa
@Strain 0.150 %,
Temperature 90.0 °C		1240 psi
@Strain 0.150 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 8.71 MPa
@Strain 0.230 %,
Temperature 150 °C		1260 psi
@Strain 0.230 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.96 MPa
@Strain 0.110 %,
Temperature 23.0 °C		1300 psi
@Strain 0.110 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 9.16 MPa
@Strain 0.180 %,
Temperature 90.0 °C		1330 psi
@Strain 0.180 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 9.23 MPa
@Strain 0.440 %,
Temperature 200 °C		1340 psi
@Strain 0.440 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 9.51 MPa
@Strain 0.130 %,
Temperature 60.0 °C		1380 psi
@Strain 0.130 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 9.64 MPa
@Strain 0.220 %,
Temperature 150 °C		1400 psi
@Strain 0.220 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.77 MPa
@Strain 0.0600 %,
Temperature -20.0 °C		1420 psi
@Strain 0.0600 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 10.05 MPa
@Strain 0.230 %,
Temperature 120 °C		1458 psi
@Strain 0.230 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.15 MPa
@Strain 0.0900 %,
Temperature 0.000 °C		1472 psi
@Strain 0.0900 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 10.4 MPa
@Strain 0.100 %,
Temperature 40.0 °C		1510 psi
@Strain 0.100 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 10.69 MPa
@Strain 0.180 %,
Temperature 60.0 °C		1550 psi
@Strain 0.180 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 10.89 MPa
@Strain 0.220 %,
Temperature 120 °C		1579 psi
@Strain 0.220 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.96 MPa
@Strain 0.0800 %,
Temperature 23.0 °C		1590 psi
@Strain 0.0800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 11.55 MPa
@Strain 0.170 %,
Temperature 40.0 °C		1675 psi
@Strain 0.170 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 11.56 MPa
@Strain 0.230 %,
Temperature 90.0 °C		1677 psi
@Strain 0.230 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 11.95 MPa
@Strain 0.220 %,
Temperature 90.0 °C		1733 psi
@Strain 0.220 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 12.06 MPa
@Strain 0.100 %,
Temperature 0.000 °C		1749 psi
@Strain 0.100 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 12.2 MPa
@Strain 0.340 %,
Temperature 180 °C		1770 psi
@Strain 0.340 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 12.53 MPa
@Strain 0.130 %,
Temperature -20.0 °C		1817 psi
@Strain 0.130 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 12.59 MPa
@Strain 0.160 %,
Temperature 23.0 °C		1826 psi
@Strain 0.160 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 13.46 MPa
@Strain 0.190 %,
Temperature 60.0 °C		1952 psi
@Strain 0.190 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 13.57 MPa
@Strain 0.240 %,
Temperature 60.0 °C		1968 psi
@Strain 0.240 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 14.39 MPa
@Strain 0.410 %,
Temperature 150 °C		2087 psi
@Strain 0.410 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 14.42 MPa
@Strain 0.130 %,
Temperature 0.000 °C		2091 psi
@Strain 0.130 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 14.68 MPa
@Strain 0.230 %,
Temperature 40.0 °C		2129 psi
@Strain 0.230 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 14.72 MPa
@Strain 0.980 %,
Temperature 200 °C		2135 psi
@Strain 0.980 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 14.74 MPa
@Strain 0.140 %,
Temperature 40.0 °C		2138 psi
@Strain 0.140 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 15.53 MPa
@Strain 0.100 %,
Temperature -20.0 °C		2252 psi
@Strain 0.100 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 15.71 MPa
@Strain 0.120 %,
Temperature 23.0 °C		2279 psi
@Strain 0.120 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 16.28 MPa
@Strain 0.220 %,
Temperature 23.0 °C		2361 psi
@Strain 0.220 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 16.97 MPa
@Strain 0.140 %,
Temperature 0.000 °C		2461 psi
@Strain 0.140 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 17.36 MPa
@Strain 0.170 %,
Temperature -20.0 °C		2518 psi
@Strain 0.170 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 17.46 MPa
@Strain 0.250 %,
Temperature 60.0 °C		2532 psi
@Strain 0.250 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 17.71 MPa
@Strain 0.420 %,
Temperature 150 °C		2569 psi
@Strain 0.420 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 18.14 MPa
@Strain 0.480 %,
Temperature 120 °C		2631 psi
@Strain 0.480 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 18.41 MPa
@Strain 1.50 %,
Temperature 200 °C		2670 psi
@Strain 1.50 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 18.44 MPa
@Strain 0.180 %,
Temperature 0.000 °C		2675 psi
@Strain 0.180 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 19.0 MPa
@Strain 0.190 %,
Temperature 40.0 °C		2760 psi
@Strain 0.190 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 19.88 MPa
@Strain 0.430 %,
Temperature 120 °C		2883 psi
@Strain 0.430 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 20.26 MPa
@Strain 0.690 %,
Temperature 180 °C		2938 psi
@Strain 0.690 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 20.28 MPa
@Strain 0.170 %,
Temperature 23.0 °C		2941 psi
@Strain 0.170 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 20.51 MPa
@Strain 0.460 %,
Temperature 90.0 °C		2975 psi
@Strain 0.460 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 21.27 MPa
@Strain 2.04 %,
Temperature 200 °C		3085 psi
@Strain 2.04 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 21.34 MPa
@Strain 0.690 %,
Temperature 150 °C		3095 psi
@Strain 0.690 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 21.44 MPa
@Strain 0.150 %,
Temperature -20.0 °C		3110 psi
@Strain 0.150 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 21.97 MPa
@Strain 0.180 %,
Temperature 0.000 °C		3186 psi
@Strain 0.180 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 21.97 MPa
@Strain 0.210 %,
Temperature -20.0 °C		3186 psi
@Strain 0.210 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 22.53 MPa
@Strain 0.220 %,
Temperature 0.000 °C		3268 psi
@Strain 0.220 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 23.05 MPa
@Strain 0.430 %,
Temperature 60.0 °C		3343 psi
@Strain 0.430 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.12 MPa
@Strain 0.460 %,
Temperature 90.0 °C		3353 psi
@Strain 0.460 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 23.13 MPa
@Strain 0.240 %,
Temperature 40.0 °C		3355 psi
@Strain 0.240 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 23.56 MPa
@Strain 2.61 %,
Temperature 200 °C		3417 psi
@Strain 2.61 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 24.72 MPa
@Strain 0.210 %,
Temperature 23.0 °C		3585 psi
@Strain 0.210 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 25.51 MPa
@Strain 0.430 %,
Temperature 40.0 °C		3700 psi
@Strain 0.430 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 25.57 MPa
@Strain 3.12 %,
Temperature 200 °C		3709 psi
@Strain 3.12 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 25.96 MPa
@Strain 1.06 %,
Temperature 180 °C		3765 psi
@Strain 1.06 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 26.05 MPa
@Strain 0.780 %,
Temperature 120 °C		3778 psi
@Strain 0.780 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 26.38 MPa
@Strain 0.380 %,
Temperature 23.0 °C		3826 psi
@Strain 0.380 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.72 MPa
@Strain 0.980 %,
Temperature 150 °C		3875 psi
@Strain 0.980 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 26.77 MPa
@Strain 0.230 %,
Temperature 0.000 °C		3883 psi
@Strain 0.230 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 27.11 MPa
@Strain 0.250 %,
Temperature -20.0 °C		3932 psi
@Strain 0.250 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 27.11 MPa
@Strain 0.190 %,
Temperature -20.0 °C		3932 psi
@Strain 0.190 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 27.32 MPa
@Strain 3.70 %,
Temperature 200 °C		3962 psi
@Strain 3.70 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 27.87 MPa
@Strain 0.750 %,
Temperature 150 °C		4042 psi
@Strain 0.750 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 28.91 MPa
@Strain 4.20 %,
Temperature 200 °C		4193 psi
@Strain 4.20 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 29.3 MPa
@Strain 0.240 %,
Temperature 23.0 °C		4250 psi
@Strain 0.240 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 29.73 MPa
@Strain 0.760 %,
Temperature 90.0 °C		4312 psi
@Strain 0.760 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 30.38 MPa
@Strain 1.43 %,
Temperature 180 °C		4406 psi
@Strain 1.43 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 30.43 MPa
@Strain 4.75 %,
Temperature 200 °C		4414 psi
@Strain 4.75 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 31.05 MPa
@Strain 1.30 %,
Temperature 150 °C		4503 psi
@Strain 1.30 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 31.8 MPa
@Strain 5.33 %,
Temperature 200 °C		4610 psi
@Strain 5.33 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 31.88 MPa
@Strain 0.770 %,
Temperature 120 °C		4624 psi
@Strain 0.770 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 32.49 MPa
@Strain 1.10 %,
Temperature 120 °C		4712 psi
@Strain 1.10 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 32.82 MPa
@Strain 0.230 %,
Temperature -20.0 °C		4760 psi
@Strain 0.230 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 33.03 MPa
@Strain 5.84 %,
Temperature 200 °C		4791 psi
@Strain 5.84 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 33.19 MPa
@Strain 0.680 %,
Temperature 60.0 °C		4814 psi
@Strain 0.680 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 33.64 MPa
@Strain 0.330 %,
Temperature 0.000 °C		4879 psi
@Strain 0.330 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 34.03 MPa
@Strain 1.82 %,
Temperature 180 °C		4936 psi
@Strain 1.82 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 34.31 MPa
@Strain 6.45 %,
Temperature 200 °C		4976 psi
@Strain 6.45 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 34.68 MPa
@Strain 1.61 %,
Temperature 150 °C		5030 psi
@Strain 1.61 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 35.2 MPa
@Strain 0.760 %,
Temperature 90.0 °C		5110 psi
@Strain 0.760 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 35.28 MPa
@Strain 0.650 %,
Temperature 40.0 °C		5117 psi
@Strain 0.650 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 35.45 MPa
@Strain 6.97 %,
Temperature 200 °C		5142 psi
@Strain 6.97 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 35.53 MPa
@Strain 0.370 %,
Temperature 40.0 °C		5153 psi
@Strain 0.370 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 35.74 MPa
@Strain 1.10 %,
Temperature 150 °C		5184 psi
@Strain 1.10 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.01 MPa
@Strain 0.560 %,
Temperature 60.0 °C		5223 psi
@Strain 0.560 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 36.68 MPa
@Strain 7.42 %,
Temperature 200 °C		5320 psi
@Strain 7.42 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 37.01 MPa
@Strain 2.21 %,
Temperature 180 °C		5368 psi
@Strain 2.21 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 37.14 MPa
@Strain 1.06 %,
Temperature 90.0 °C		5387 psi
@Strain 1.06 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 37.31 MPa
@Strain 0.580 %,
Temperature 23.0 °C		5411 psi
@Strain 0.580 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 37.75 MPa
@Strain 1.42 %,
Temperature 120 °C		5475 psi
@Strain 1.42 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 37.8 MPa
@Strain 7.96 %,
Temperature 200 °C		5480 psi
@Strain 7.96 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 37.88 MPa
@Strain 1.93 %,
Temperature 150 °C		5494 psi
@Strain 1.93 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 38.55 MPa
@Strain 0.330 %,
Temperature 0.000 °C		5591 psi
@Strain 0.330 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 38.9 MPa
@Strain 8.60 %,
Temperature 200 °C		5640 psi
@Strain 8.60 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 39.58 MPa
@Strain 2.60 %,
Temperature 180 °C		5741 psi
@Strain 2.60 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 39.9 MPa
@Strain 9.21 %,
Temperature 200 °C		5790 psi
@Strain 9.21 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 40.58 MPa
@Strain 1.09 %,
Temperature 120 °C		5886 psi
@Strain 1.09 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.63 MPa
@Strain 2.26 %,
Temperature 150 °C		5893 psi
@Strain 2.26 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 40.88 MPa
@Strain 9.68 %,
Temperature 200 °C		5929 psi
@Strain 9.68 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 40.97 MPa
@Strain 0.910 %,
Temperature 60.0 °C		5942 psi
@Strain 0.910 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 41.33 MPa
@Strain 1.43 %,
Temperature 150 °C		5994 psi
@Strain 1.43 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.82 MPa
@Strain 2.98 %,
Temperature 180 °C		6065 psi
@Strain 2.98 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 41.84 MPa
@Strain 10.14 %,
Temperature 200 °C		6068 psi
@Strain 10.14 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 42.09 MPa
@Strain 1.73 %,
Temperature 120 °C		6105 psi
@Strain 1.73 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 42.67 MPa
@Strain 10.78 %,
Temperature 200 °C		6189 psi
@Strain 10.78 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 42.83 MPa
@Strain 0.850 %,
Temperature 40.0 °C		6212 psi
@Strain 0.850 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 43.01 MPa
@Strain 1.35 %,
Temperature 90.0 °C		6238 psi
@Strain 1.35 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 43.05 MPa
@Strain 2.59 %,
Temperature 150 °C		6244 psi
@Strain 2.59 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 43.21 MPa
@Strain 12.23 %,
Temperature 200 °C		6267 psi
@Strain 12.23 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 43.3 MPa
@Strain 11.45 %,
Temperature 200 °C		6280 psi
@Strain 11.45 %,
Temperature 392 °F		DAM; ISO 11403-1/-2
 43.85 MPa
@Strain 3.37 %,
Temperature 180 °C		6360 psi
@Strain 3.37 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 45.03 MPa
@Strain 1.06 %,
Temperature 90.0 °C		6531 psi
@Strain 1.06 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 45.1 MPa
@Strain 2.91 %,
Temperature 150 °C		6540 psi
@Strain 2.91 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 45.77 MPa
@Strain 3.76 %,
Temperature 180 °C		6638 psi
@Strain 3.76 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 45.87 MPa
@Strain 2.04 %,
Temperature 120 °C		6653 psi
@Strain 2.04 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 45.92 MPa
@Strain 0.760 %,
Temperature 23.0 °C		6660 psi
@Strain 0.760 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 46.42 MPa
@Strain 0.420 %,
Temperature -20.0 °C		6733 psi
@Strain 0.420 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 46.43 MPa
@Strain 0.400 %,
Temperature 23.0 °C		6734 psi
@Strain 0.400 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 46.54 MPa
@Strain 1.80 %,
Temperature 150 °C		6750 psi
@Strain 1.80 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.96 MPa
@Strain 3.23 %,
Temperature 150 °C		6811 psi
@Strain 3.23 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 47.37 MPa
@Strain 1.13 %,
Temperature 60.0 °C		6870 psi
@Strain 1.13 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 47.52 MPa
@Strain 4.16 %,
Temperature 180 °C		6892 psi
@Strain 4.16 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 47.95 MPa
@Strain 1.63 %,
Temperature 90.0 °C		6955 psi
@Strain 1.63 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 47.99 MPa
@Strain 1.42 %,
Temperature 120 °C		6960 psi
@Strain 1.42 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 48.68 MPa
@Strain 3.56 %,
Temperature 150 °C		7060 psi
@Strain 3.56 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 48.94 MPa
@Strain 0.810 %,
Temperature 60.0 °C		7098 psi
@Strain 0.810 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.14 MPa
@Strain 4.51 %,
Temperature 180 °C		7127 psi
@Strain 4.51 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 49.22 MPa
@Strain 2.35 %,
Temperature 120 °C		7139 psi
@Strain 2.35 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 49.75 MPa
@Strain 0.530 %,
Temperature 40.0 °C		7216 psi
@Strain 0.530 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 49.9 MPa
@Strain 1.05 %,
Temperature 40.0 °C		7240 psi
@Strain 1.05 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 50.19 MPa
@Strain 3.89 %,
Temperature 150 °C		7279 psi
@Strain 3.89 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 50.56 MPa
@Strain 4.93 %,
Temperature 180 °C		7333 psi
@Strain 4.93 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 50.79 MPa
@Strain 2.17 %,
Temperature 150 °C		7366 psi
@Strain 2.17 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 51.59 MPa
@Strain 4.22 %,
Temperature 150 °C		7483 psi
@Strain 4.22 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 51.98 MPa
@Strain 5.32 %,
Temperature 180 °C		7539 psi
@Strain 5.32 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 52.16 MPa
@Strain 0.540 %,
Temperature 0.000 °C		7565 psi
@Strain 0.540 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 52.16 MPa
@Strain 0.400 %,
Temperature -20.0 °C		7565 psi
@Strain 0.400 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 52.26 MPa
@Strain 2.67 %,
Temperature 120 °C		7580 psi
@Strain 2.67 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 52.64 MPa
@Strain 1.93 %,
Temperature 90.0 °C		7635 psi
@Strain 1.93 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 52.85 MPa
@Strain 4.52 %,
Temperature 150 °C		7665 psi
@Strain 4.52 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 53.23 MPa
@Strain 5.75 %,
Temperature 180 °C		7720 psi
@Strain 5.75 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 53.38 MPa
@Strain 1.37 %,
Temperature 60.0 °C		7742 psi
@Strain 1.37 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 53.91 MPa
@Strain 0.940 %,
Temperature 23.0 °C		7819 psi
@Strain 0.940 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 53.93 MPa
@Strain 4.87 %,
Temperature 150 °C		7822 psi
@Strain 4.87 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 53.98 MPa
@Strain 1.75 %,
Temperature 120 °C		7829 psi
@Strain 1.75 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.99 MPa
@Strain 1.37 %,
Temperature 90.0 °C		7831 psi
@Strain 1.37 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 54.35 MPa
@Strain 6.19 %,
Temperature 180 °C		7883 psi
@Strain 6.19 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 54.69 MPa
@Strain 2.57 %,
Temperature 150 °C		7932 psi
@Strain 2.57 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 54.91 MPa
@Strain 5.25 %,
Temperature 150 °C		7964 psi
@Strain 5.25 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 54.99 MPa
@Strain 3.00 %,
Temperature 120 °C		7976 psi
@Strain 3.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 55.41 MPa
@Strain 6.62 %,
Temperature 180 °C		8037 psi
@Strain 6.62 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 55.79 MPa
@Strain 5.63 %,
Temperature 150 °C		8092 psi
@Strain 5.63 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 55.97 MPa
@Strain 0.490 %,
Temperature 0.000 °C		8118 psi
@Strain 0.490 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 56.47 MPa
@Strain 7.05 %,
Temperature 180 °C		8190 psi
@Strain 7.05 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 56.53 MPa
@Strain 6.02 %,
Temperature 150 °C		8199 psi
@Strain 6.02 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 56.8 MPa
@Strain 2.23 %,
Temperature 90.0 °C		8240 psi
@Strain 2.23 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 56.91 MPa
@Strain 6.82 %,
Temperature 150 °C		8254 psi
@Strain 6.82 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 56.94 MPa
@Strain 1.28 %,
Temperature 40.0 °C		8258 psi
@Strain 1.28 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 57.09 MPa
@Strain 6.40 %,
Temperature 150 °C		8280 psi
@Strain 6.40 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 57.4 MPa
@Strain 7.47 %,
Temperature 180 °C		8330 psi
@Strain 7.47 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 57.47 MPa
@Strain 3.34 %,
Temperature 120 °C		8335 psi
@Strain 3.34 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 57.66 MPa
@Strain 8.34 %,
Temperature 180 °C		8363 psi
@Strain 8.34 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 57.9 MPa
@Strain 2.96 %,
Temperature 150 °C		8400 psi
@Strain 2.96 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 58.23 MPa
@Strain 7.88 %,
Temperature 180 °C		8446 psi
@Strain 7.88 %,
Temperature 356 °F		DAM; ISO 11403-1/-2
 58.94 MPa
@Strain 1.61 %,
Temperature 60.0 °C		8549 psi
@Strain 1.61 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 59.15 MPa
@Strain 2.09 %,
Temperature 120 °C		8579 psi
@Strain 2.09 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 59.64 MPa
@Strain 3.69 %,
Temperature 120 °C		8650 psi
@Strain 3.69 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 60.07 MPa
@Strain 1.06 %,
Temperature 60.0 °C		8712 psi
@Strain 1.06 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 60.3 MPa
@Strain 2.52 %,
Temperature 90.0 °C		8750 psi
@Strain 2.52 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 60.9 MPa
@Strain 3.36 %,
Temperature 150 °C		8830 psi
@Strain 3.36 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.36 MPa
@Strain 0.550 %,
Temperature -20.0 °C		8900 psi
@Strain 0.550 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 61.37 MPa
@Strain 1.68 %,
Temperature 90.0 °C		8901 psi
@Strain 1.68 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 61.61 MPa
@Strain 4.04 %,
Temperature 120 °C		8936 psi
@Strain 4.04 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 61.92 MPa
@Strain 0.540 %,
Temperature 23.0 °C		8981 psi
@Strain 0.540 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 62.05 MPa
@Strain 1.16 %,
Temperature 23.0 °C		9000 psi
@Strain 1.16 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 63.17 MPa
@Strain 0.690 %,
Temperature 40.0 °C		9162 psi
@Strain 0.690 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 63.34 MPa
@Strain 4.36 %,
Temperature 120 °C		9187 psi
@Strain 4.36 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 63.52 MPa
@Strain 3.75 %,
Temperature 150 °C		9213 psi
@Strain 3.75 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.66 MPa
@Strain 2.84 %,
Temperature 90.0 °C		9233 psi
@Strain 2.84 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 63.75 MPa
@Strain 1.53 %,
Temperature 40.0 °C		9246 psi
@Strain 1.53 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 63.92 MPa
@Strain 2.46 %,
Temperature 120 °C		9271 psi
@Strain 2.46 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 64.19 MPa
@Strain 1.88 %,
Temperature 60.0 °C		9310 psi
@Strain 1.88 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 64.62 MPa
@Strain 0.690 %,
Temperature 0.000 °C		9372 psi
@Strain 0.690 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 64.88 MPa
@Strain 4.73 %,
Temperature 120 °C		9410 psi
@Strain 4.73 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 66.03 MPa
@Strain 4.13 %,
Temperature 150 °C		9577 psi
@Strain 4.13 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 66.26 MPa
@Strain 5.14 %,
Temperature 120 °C		9610 psi
@Strain 5.14 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 66.78 MPa
@Strain 3.19 %,
Temperature 90.0 °C		9686 psi
@Strain 3.19 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 67.45 MPa
@Strain 5.56 %,
Temperature 120 °C		9783 psi
@Strain 5.56 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 68.04 MPa
@Strain 2.01 %,
Temperature 90.0 °C		9868 psi
@Strain 2.01 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 68.08 MPa
@Strain 7.42 %,
Temperature 120 °C		9874 psi
@Strain 7.42 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 68.24 MPa
@Strain 2.83 %,
Temperature 120 °C		9897 psi
@Strain 2.83 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 68.28 MPa
@Strain 4.57 %,
Temperature 150 °C		9903 psi
@Strain 4.57 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 68.45 MPa
@Strain 6.00 %,
Temperature 120 °C		9928 psi
@Strain 6.00 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 69.22 MPa
@Strain 6.43 %,
Temperature 120 °C		10040 psi
@Strain 6.43 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 69.23 MPa
@Strain 2.17 %,
Temperature 60.0 °C		10040 psi
@Strain 2.17 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 69.24 MPa
@Strain 1.31 %,
Temperature 60.0 °C		10040 psi
@Strain 1.31 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 69.53 MPa
@Strain 3.55 %,
Temperature 90.0 °C		10080 psi
@Strain 3.55 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 69.74 MPa
@Strain 6.88 %,
Temperature 120 °C		10110 psi
@Strain 6.88 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 69.79 MPa
@Strain 1.38 %,
Temperature 23.0 °C		10120 psi
@Strain 1.38 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 70.23 MPa
@Strain 1.80 %,
Temperature 40.0 °C		10190 psi
@Strain 1.80 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 70.26 MPa
@Strain 5.00 %,
Temperature 150 °C		10190 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 70.53 MPa
@Strain 0.620 %,
Temperature 0.000 °C		10230 psi
@Strain 0.620 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 70.99 MPa
@Strain 0.560 %,
Temperature -20.0 °C		10300 psi
@Strain 0.560 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 71.85 MPa
@Strain 3.91 %,
Temperature 90.0 °C		10420 psi
@Strain 3.91 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 72.12 MPa
@Strain 5.48 %,
Temperature 150 °C		10460 psi
@Strain 5.48 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 72.15 MPa
@Strain 3.24 %,
Temperature 120 °C		10460 psi
@Strain 3.24 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 73.26 MPa
@Strain 0.650 %,
Temperature -20.0 °C		10630 psi
@Strain 0.650 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 73.73 MPa
@Strain 5.94 %,
Temperature 150 °C		10690 psi
@Strain 5.94 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 73.77 MPa
@Strain 2.47 %,
Temperature 60.0 °C		10700 psi
@Strain 2.47 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 73.95 MPa
@Strain 4.24 %,
Temperature 90.0 °C		10730 psi
@Strain 4.24 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 74.02 MPa
@Strain 2.36 %,
Temperature 90.0 °C		10740 psi
@Strain 2.36 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 74.79 MPa
@Strain 0.840 %,
Temperature 40.0 °C		10850 psi
@Strain 0.840 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 75.23 MPa
@Strain 6.41 %,
Temperature 150 °C		10910 psi
@Strain 6.41 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 75.42 MPa
@Strain 0.830 %,
Temperature 0.000 °C		10940 psi
@Strain 0.830 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 75.64 MPa
@Strain 3.64 %,
Temperature 120 °C		10970 psi
@Strain 3.64 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 75.75 MPa
@Strain 4.63 %,
Temperature 90.0 °C		10990 psi
@Strain 4.63 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 76.29 MPa
@Strain 2.08 %,
Temperature 40.0 °C		11060 psi
@Strain 2.08 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 76.34 MPa
@Strain 0.670 %,
Temperature 23.0 °C		11070 psi
@Strain 0.670 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 76.54 MPa
@Strain 6.87 %,
Temperature 150 °C		11100 psi
@Strain 6.87 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 77.0 MPa
@Strain 1.61 %,
Temperature 23.0 °C		11200 psi
@Strain 1.61 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 77.34 MPa
@Strain 5.07 %,
Temperature 90.0 °C		11220 psi
@Strain 5.07 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 77.59 MPa
@Strain 7.32 %,
Temperature 150 °C		11250 psi
@Strain 7.32 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 77.73 MPa
@Strain 1.55 %,
Temperature 60.0 °C		11270 psi
@Strain 1.55 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 77.89 MPa
@Strain 2.80 %,
Temperature 60.0 °C		11300 psi
@Strain 2.80 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 78.52 MPa
@Strain 7.82 %,
Temperature 150 °C		11390 psi
@Strain 7.82 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 78.6 MPa
@Strain 5.48 %,
Temperature 90.0 °C		11400 psi
@Strain 5.48 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 78.76 MPa
@Strain 8.94 %,
Temperature 150 °C		11420 psi
@Strain 8.94 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 78.78 MPa
@Strain 4.05 %,
Temperature 120 °C		11430 psi
@Strain 4.05 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 79.21 MPa
@Strain 8.32 %,
Temperature 150 °C		11490 psi
@Strain 8.32 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 79.39 MPa
@Strain 2.71 %,
Temperature 90.0 °C		11510 psi
@Strain 2.71 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 79.72 MPa
@Strain 5.94 %,
Temperature 90.0 °C		11560 psi
@Strain 5.94 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 80.15 MPa
@Strain 7.41 %,
Temperature 90.0 °C		11620 psi
@Strain 7.41 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 80.56 MPa
@Strain 6.42 %,
Temperature 90.0 °C		11680 psi
@Strain 6.42 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 81.08 MPa
@Strain 6.86 %,
Temperature 90.0 °C		11760 psi
@Strain 6.86 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 81.6 MPa
@Strain 4.46 %,
Temperature 120 °C		11800 psi
@Strain 4.46 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 81.62 MPa
@Strain 3.14 %,
Temperature 60.0 °C		11840 psi
@Strain 3.14 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 81.87 MPa
@Strain 2.38 %,
Temperature 40.0 °C		11870 psi
@Strain 2.38 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 83.18 MPa
@Strain 0.730 %,
Temperature 0.000 °C		12060 psi
@Strain 0.730 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 84.09 MPa
@Strain 4.90 %,
Temperature 120 °C		12200 psi
@Strain 4.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 84.17 MPa
@Strain 1.87 %,
Temperature 23.0 °C		12210 psi
@Strain 1.87 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 84.28 MPa
@Strain 3.09 %,
Temperature 90.0 °C		12220 psi
@Strain 3.09 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 84.86 MPa
@Strain 3.47 %,
Temperature 60.0 °C		12310 psi
@Strain 3.47 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 85.22 MPa
@Strain 0.770 %,
Temperature -20.0 °C		12360 psi
@Strain 0.770 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 85.27 MPa
@Strain 1.00 %,
Temperature 40.0 °C		12370 psi
@Strain 1.00 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 85.34 MPa
@Strain 0.990 %,
Temperature 0.000 °C		12380 psi
@Strain 0.990 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 85.43 MPa
@Strain 1.81 %,
Temperature 60.0 °C		12390 psi
@Strain 1.81 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 85.97 MPa
@Strain 0.690 %,
Temperature -20.0 °C		12470 psi
@Strain 0.690 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 86.35 MPa
@Strain 5.39 %,
Temperature 120 °C		12520 psi
@Strain 5.39 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 87.0 MPa
@Strain 2.71 %,
Temperature 40.0 °C		12600 psi
@Strain 2.71 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 87.64 MPa
@Strain 3.85 %,
Temperature 60.0 °C		12710 psi
@Strain 3.85 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 88.29 MPa
@Strain 5.90 %,
Temperature 120 °C		12810 psi
@Strain 5.90 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 88.65 MPa
@Strain 3.49 %,
Temperature 90.0 °C		12860 psi
@Strain 3.49 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 89.84 MPa
@Strain 0.800 %,
Temperature 23.0 °C		13030 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.99 MPa
@Strain 6.41 %,
Temperature 120 °C		13050 psi
@Strain 6.41 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 90.02 MPa
@Strain 4.30 %,
Temperature 60.0 °C		13060 psi
@Strain 4.30 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 90.74 MPa
@Strain 2.15 %,
Temperature 23.0 °C		13160 psi
@Strain 2.15 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 91.49 MPa
@Strain 3.06 %,
Temperature 40.0 °C		13270 psi
@Strain 3.06 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 91.51 MPa
@Strain 6.93 %,
Temperature 120 °C		13270 psi
@Strain 6.93 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 91.96 MPa
@Strain 4.75 %,
Temperature 60.0 °C		13340 psi
@Strain 4.75 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 92.59 MPa
@Strain 3.90 %,
Temperature 90.0 °C		13430 psi
@Strain 3.90 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 92.72 MPa
@Strain 7.45 %,
Temperature 120 °C		13450 psi
@Strain 7.45 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 92.74 MPa
@Strain 2.09 %,
Temperature 60.0 °C		13450 psi
@Strain 2.09 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 93.55 MPa
@Strain 5.21 %,
Temperature 60.0 °C		13570 psi
@Strain 5.21 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 93.73 MPa
@Strain 7.98 %,
Temperature 120 °C		13590 psi
@Strain 7.98 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 94.07 MPa
@Strain 9.25 %,
Temperature 120 °C		13640 psi
@Strain 9.25 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 94.28 MPa
@Strain 7.42 %,
Temperature 60.0 °C		13670 psi
@Strain 7.42 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 94.43 MPa
@Strain 8.57 %,
Temperature 120 °C		13700 psi
@Strain 8.57 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 94.78 MPa
@Strain 5.71 %,
Temperature 60.0 °C		13750 psi
@Strain 5.71 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 95.07 MPa
@Strain 1.15 %,
Temperature 0.000 °C		13790 psi
@Strain 1.15 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 95.19 MPa
@Strain 1.16 %,
Temperature 40.0 °C		13810 psi
@Strain 1.16 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 95.45 MPa
@Strain 3.38 %,
Temperature 40.0 °C		13840 psi
@Strain 3.38 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 95.64 MPa
@Strain 6.20 %,
Temperature 60.0 °C		13870 psi
@Strain 6.20 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 95.99 MPa
@Strain 4.31 %,
Temperature 90.0 °C		13920 psi
@Strain 4.31 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 96.08 MPa
@Strain 6.74 %,
Temperature 60.0 °C		13940 psi
@Strain 6.74 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 96.23 MPa
@Strain 0.860 %,
Temperature 0.000 °C		13960 psi
@Strain 0.860 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.54 MPa
@Strain 2.42 %,
Temperature 23.0 °C		14000 psi
@Strain 2.42 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 97.86 MPa
@Strain 0.900 %,
Temperature -20.0 °C		14190 psi
@Strain 0.900 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 98.74 MPa
@Strain 3.78 %,
Temperature 40.0 °C		14320 psi
@Strain 3.78 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 98.96 MPa
@Strain 4.79 %,
Temperature 90.0 °C		14350 psi
@Strain 4.79 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 99.3 MPa
@Strain 2.38 %,
Temperature 60.0 °C		14400 psi
@Strain 2.38 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 100.86 MPa
@Strain 0.840 %,
Temperature -20.0 °C		14629 psi
@Strain 0.840 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 101.24 MPa
@Strain 0.930 %,
Temperature 23.0 °C		14684 psi
@Strain 0.930 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 101.44 MPa
@Strain 4.22 %,
Temperature 40.0 °C		14713 psi
@Strain 4.22 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 101.51 MPa
@Strain 5.30 %,
Temperature 90.0 °C		14723 psi
@Strain 5.30 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 102.22 MPa
@Strain 2.73 %,
Temperature 23.0 °C		14826 psi
@Strain 2.73 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 103.59 MPa
@Strain 5.81 %,
Temperature 90.0 °C		15024 psi
@Strain 5.81 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 103.6 MPa
@Strain 4.68 %,
Temperature 40.0 °C		15030 psi
@Strain 4.68 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 104.32 MPa
@Strain 1.31 %,
Temperature 0.000 °C		15130 psi
@Strain 1.31 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 104.43 MPa
@Strain 1.32 %,
Temperature 40.0 °C		15146 psi
@Strain 1.32 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 105.38 MPa
@Strain 5.18 %,
Temperature 40.0 °C		15284 psi
@Strain 5.18 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 105.38 MPa
@Strain 2.68 %,
Temperature 60.0 °C		15284 psi
@Strain 2.68 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 105.39 MPa
@Strain 6.36 %,
Temperature 90.0 °C		15286 psi
@Strain 6.36 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 105.6 MPa
@Strain 7.51 %,
Temperature 40.0 °C		15320 psi
@Strain 7.51 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 106.63 MPa
@Strain 5.67 %,
Temperature 40.0 °C		15465 psi
@Strain 5.67 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 106.82 MPa
@Strain 6.91 %,
Temperature 90.0 °C		15493 psi
@Strain 6.91 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 107.18 MPa
@Strain 3.05 %,
Temperature 23.0 °C		15545 psi
@Strain 3.05 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 107.49 MPa
@Strain 6.20 %,
Temperature 40.0 °C		15590 psi
@Strain 6.20 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 107.84 MPa
@Strain 6.80 %,
Temperature 40.0 °C		15641 psi
@Strain 6.80 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 107.95 MPa
@Strain 7.47 %,
Temperature 90.0 °C		15657 psi
@Strain 7.47 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 108.46 MPa
@Strain 9.42 %,
Temperature 90.0 °C		15731 psi
@Strain 9.42 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 108.8 MPa
@Strain 8.06 %,
Temperature 90.0 °C		15780 psi
@Strain 8.06 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 108.95 MPa
@Strain 0.990 %,
Temperature 0.000 °C		15802 psi
@Strain 0.990 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 109.19 MPa
@Strain 8.70 %,
Temperature 90.0 °C		15837 psi
@Strain 8.70 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 110.27 MPa
@Strain 1.04 %,
Temperature -20.0 °C		15993 psi
@Strain 1.04 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 110.88 MPa
@Strain 3.01 %,
Temperature 60.0 °C		16082 psi
@Strain 3.01 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 111.42 MPa
@Strain 3.43 %,
Temperature 23.0 °C		16160 psi
@Strain 3.43 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 112.55 MPa
@Strain 1.05 %,
Temperature 23.0 °C		16324 psi
@Strain 1.05 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 113.04 MPa
@Strain 1.49 %,
Temperature 0.000 °C		16395 psi
@Strain 1.49 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 113.33 MPa
@Strain 1.49 %,
Temperature 40.0 °C		16437 psi
@Strain 1.49 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 114.84 MPa
@Strain 3.84 %,
Temperature 23.0 °C		16656 psi
@Strain 3.84 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 115.73 MPa
@Strain 3.35 %,
Temperature 60.0 °C		16785 psi
@Strain 3.35 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 116.05 MPa
@Strain 0.980 %,
Temperature -20.0 °C		16832 psi
@Strain 0.980 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 117.4 MPa
@Strain 4.24 %,
Temperature 23.0 °C		17030 psi
@Strain 4.24 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 119.4 MPa
@Strain 4.70 %,
Temperature 23.0 °C		17320 psi
@Strain 4.70 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 119.89 MPa
@Strain 3.72 %,
Temperature 60.0 °C		17389 psi
@Strain 3.72 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 120.28 MPa
@Strain 7.05 %,
Temperature 23.0 °C		17445 psi
@Strain 7.05 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 120.82 MPa
@Strain 5.19 %,
Temperature 23.0 °C		17523 psi
@Strain 5.19 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 121.35 MPa
@Strain 1.67 %,
Temperature 0.000 °C		17600 psi
@Strain 1.67 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 121.66 MPa
@Strain 5.75 %,
Temperature 23.0 °C		17645 psi
@Strain 5.75 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 121.8 MPa
@Strain 1.19 %,
Temperature -20.0 °C		17670 psi
@Strain 1.19 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 121.83 MPa
@Strain 1.69 %,
Temperature 40.0 °C		17670 psi
@Strain 1.69 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 121.88 MPa
@Strain 1.13 %,
Temperature 0.000 °C		17677 psi
@Strain 1.13 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 121.95 MPa
@Strain 6.34 %,
Temperature 23.0 °C		17687 psi
@Strain 6.34 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 123.15 MPa
@Strain 1.18 %,
Temperature 23.0 °C		17861 psi
@Strain 1.18 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 123.25 MPa
@Strain 4.09 %,
Temperature 60.0 °C		17876 psi
@Strain 4.09 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 125.93 MPa
@Strain 4.54 %,
Temperature 60.0 °C		18265 psi
@Strain 4.54 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 128.04 MPa
@Strain 5.01 %,
Temperature 60.0 °C		18571 psi
@Strain 5.01 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 129.33 MPa
@Strain 1.88 %,
Temperature 0.000 °C		18758 psi
@Strain 1.88 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 129.56 MPa
@Strain 5.54 %,
Temperature 60.0 °C		18791 psi
@Strain 5.54 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 129.58 MPa
@Strain 1.90 %,
Temperature 40.0 °C		18794 psi
@Strain 1.90 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 130.55 MPa
@Strain 7.82 %,
Temperature 60.0 °C		18935 psi
@Strain 7.82 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 130.62 MPa
@Strain 6.08 %,
Temperature 60.0 °C		18945 psi
@Strain 6.08 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 131.29 MPa
@Strain 1.13 %,
Temperature -20.0 °C		19042 psi
@Strain 1.13 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 131.33 MPa
@Strain 6.62 %,
Temperature 60.0 °C		19048 psi
@Strain 6.62 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 131.56 MPa
@Strain 7.19 %,
Temperature 60.0 °C		19081 psi
@Strain 7.19 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 132.76 MPa
@Strain 1.33 %,
Temperature -20.0 °C		19255 psi
@Strain 1.33 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 133.04 MPa
@Strain 1.30 %,
Temperature 23.0 °C		19296 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 134.08 MPa
@Strain 1.27 %,
Temperature 0.000 °C		19447 psi
@Strain 1.27 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 136.66 MPa
@Strain 2.08 %,
Temperature 0.000 °C		19821 psi
@Strain 2.08 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 136.83 MPa
@Strain 2.12 %,
Temperature 40.0 °C		19846 psi
@Strain 2.12 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 142.92 MPa
@Strain 1.44 %,
Temperature 23.0 °C		20729 psi
@Strain 1.44 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 143.36 MPa
@Strain 2.36 %,
Temperature 40.0 °C		20793 psi
@Strain 2.36 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 143.42 MPa
@Strain 2.30 %,
Temperature 0.000 °C		20801 psi
@Strain 2.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 143.73 MPa
@Strain 1.49 %,
Temperature -20.0 °C		20846 psi
@Strain 1.49 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 145.29 MPa
@Strain 1.40 %,
Temperature 0.000 °C		21073 psi
@Strain 1.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 145.84 MPa
@Strain 1.30 %,
Temperature -20.0 °C		21152 psi
@Strain 1.30 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 149.11 MPa
@Strain 2.64 %,
Temperature 40.0 °C		21627 psi
@Strain 2.64 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 149.69 MPa
@Strain 2.54 %,
Temperature 0.000 °C		21711 psi
@Strain 2.54 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 152.88 MPa
@Strain 1.60 %,
Temperature 23.0 °C		22173 psi
@Strain 1.60 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 153.76 MPa
@Strain 2.94 %,
Temperature 40.0 °C		22301 psi
@Strain 2.94 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 154.17 MPa
@Strain 1.65 %,
Temperature -20.0 °C		22361 psi
@Strain 1.65 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 155.12 MPa
@Strain 2.80 %,
Temperature 0.000 °C		22498 psi
@Strain 2.80 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 156.52 MPa
@Strain 1.55 %,
Temperature 0.000 °C		22701 psi
@Strain 1.55 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 157.42 MPa
@Strain 3.28 %,
Temperature 40.0 °C		22832 psi
@Strain 3.28 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 159.32 MPa
@Strain 5.07 %,
Temperature 40.0 °C		23107 psi
@Strain 5.07 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 159.54 MPa
@Strain 3.10 %,
Temperature 0.000 °C		23139 psi
@Strain 3.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 159.7 MPa
@Strain 3.65 %,
Temperature 40.0 °C		23160 psi
@Strain 3.65 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 159.95 MPa
@Strain 1.46 %,
Temperature -20.0 °C		23199 psi
@Strain 1.46 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 160.67 MPa
@Strain 4.05 %,
Temperature 40.0 °C		23303 psi
@Strain 4.05 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 160.68 MPa
@Strain 4.51 %,
Temperature 40.0 °C		23305 psi
@Strain 4.51 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 161.31 MPa
@Strain 4.85 %,
Temperature 0.000 °C		23396 psi
@Strain 4.85 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 162.12 MPa
@Strain 1.75 %,
Temperature 23.0 °C		23514 psi
@Strain 1.75 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 162.63 MPa
@Strain 3.42 %,
Temperature 0.000 °C		23588 psi
@Strain 3.42 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 164 MPa
@Strain 4.30 %,
Temperature 0.000 °C		23800 psi
@Strain 4.30 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 164.12 MPa
@Strain 3.82 %,
Temperature 0.000 °C		23804 psi
@Strain 3.82 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 164.28 MPa
@Strain 1.83 %,
Temperature -20.0 °C		23827 psi
@Strain 1.83 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 167.43 MPa
@Strain 1.71 %,
Temperature 0.000 °C		24284 psi
@Strain 1.71 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 171.1 MPa
@Strain 1.94 %,
Temperature 23.0 °C		24820 psi
@Strain 1.94 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 173.69 MPa
@Strain 1.62 %,
Temperature -20.0 °C		25192 psi
@Strain 1.62 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 174.04 MPa
@Strain 2.02 %,
Temperature -20.0 °C		25242 psi
@Strain 2.02 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 178.11 MPa
@Strain 1.87 %,
Temperature 0.000 °C		25833 psi
@Strain 1.87 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 179.12 MPa
@Strain 2.12 %,
Temperature 23.0 °C		25979 psi
@Strain 2.12 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 182.85 MPa
@Strain 2.22 %,
Temperature -20.0 °C		26520 psi
@Strain 2.22 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 186.46 MPa
@Strain 2.34 %,
Temperature 23.0 °C		27044 psi
@Strain 2.34 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 186.9 MPa
@Strain 1.80 %,
Temperature -20.0 °C		27110 psi
@Strain 1.80 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 188.32 MPa
@Strain 2.05 %,
Temperature 0.000 °C		27314 psi
@Strain 2.05 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 190.8 MPa
@Strain 2.43 %,
Temperature -20.0 °C		27670 psi
@Strain 2.43 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 192.96 MPa
@Strain 2.59 %,
Temperature 23.0 °C		27987 psi
@Strain 2.59 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 197.94 MPa
@Strain 2.88 %,
Temperature 23.0 °C		28709 psi
@Strain 2.88 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 198.09 MPa
@Strain 2.67 %,
Temperature -20.0 °C		28731 psi
@Strain 2.67 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 198.14 MPa
@Strain 2.25 %,
Temperature 0.000 °C		28738 psi
@Strain 2.25 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 199.33 MPa
@Strain 1.98 %,
Temperature -20.0 °C		28910 psi
@Strain 1.98 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 199.44 MPa
@Strain 3.72 %,
Temperature 23.0 °C		28926 psi
@Strain 3.72 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 200.78 MPa
@Strain 3.22 %,
Temperature 23.0 °C		29121 psi
@Strain 3.22 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 204.06 MPa
@Strain 2.88 %,
Temperature -20.0 °C		29596 psi
@Strain 2.88 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 206.92 MPa
@Strain 2.46 %,
Temperature 0.000 °C		30011 psi
@Strain 2.46 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 208.19 MPa
@Strain 3.20 %,
Temperature -20.0 °C		30195 psi
@Strain 3.20 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 208.63 MPa
@Strain 3.67 %,
Temperature -20.0 °C		30259 psi
@Strain 3.67 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 211.56 MPa
@Strain 2.17 %,
Temperature -20.0 °C		30684 psi
@Strain 2.17 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 214.64 MPa
@Strain 2.65 %,
Temperature 0.000 °C		31131 psi
@Strain 2.65 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 221.59 MPa
@Strain 2.89 %,
Temperature 0.000 °C		32139 psi
@Strain 2.89 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 223.08 MPa
@Strain 2.38 %,
Temperature -20.0 °C		32355 psi
@Strain 2.38 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 226.74 MPa
@Strain 3.21 %,
Temperature 0.000 °C		32886 psi
@Strain 3.21 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 228.31 MPa
@Strain 3.63 %,
Temperature 0.000 °C		33114 psi
@Strain 3.63 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 233.99 MPa
@Strain 2.54 %,
Temperature -20.0 °C		33937 psi
@Strain 2.54 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 244.28 MPa
@Strain 2.77 %,
Temperature -20.0 °C		35430 psi
@Strain 2.77 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 253.45 MPa
@Strain 3.01 %,
Temperature -20.0 °C		36760 psi
@Strain 3.01 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 261.7 MPa
@Strain 3.29 %,
Temperature -20.0 °C		37960 psi
@Strain 3.29 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 268.29 MPa
@Strain 3.59 %,
Temperature -20.0 °C		38912 psi
@Strain 3.59 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
Elongation at Break  3.5 %
@Temperature 23.0 °C		3.5 %
@Temperature 73.4 °F		DAM; ISO 527
 7.0 %
@Temperature 23.0 °C		7.0 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  6.50 GPa
@Temperature 23.0 °C		943 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 11.5 GPa
@Temperature 23.0 °C		1670 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength 309 MPa
@Temperature 23.0 °C		44800 psi
@Temperature 73.4 °F		DAM; ISO 178
Flexural Modulus 10.1 GPa
@Temperature 23.0 °C		1460 ksi
@Temperature 73.4 °F		DAM; ISO 178
Charpy Impact Unnotched  8.10 J/cm²
@Temperature -30.0 °C		38.5 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 8.30 J/cm²
@Temperature -30.0 °C		39.5 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 9.30 J/cm²
@Temperature 23.0 °C		44.3 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
 9.60 J/cm²
@Temperature 23.0 °C		45.7 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  1.30 J/cm²
@Temperature -30.0 °C		6.19 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 1.50 J/cm²
@Temperature 23.0 °C		7.14 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  7.10e+13 ohm-cm
@Temperature 23.0 °C		7.10e+13 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.40e+16 ohm-cm
@Temperature 23.0 °C		1.40e+16 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Surface Resistance  6.10e+13 ohm
@Temperature 23.0 °C		6.10e+13 ohm
@Temperature 73.4 °F		DAM; IEC 60093
 1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		50%RH; IEC 60093
Comparative Tracking Index 550 V
@Temperature 23.0 °C		550 V
@Temperature 73.4 °F		DAM; IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		5.56 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 220 °C428 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 212 °C414 °FDAM; ISO 75-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 224 °C435 °F10°C/min; DAM; ISO 11357-1/-3
 270 °C518 °FDAM; Optimum
 260 - 280 °C500 - 536 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AppearanceBlack ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesFlow, GoodDAM
 WeldableDAM
FillerGlass ReinforcedDAM
FormsPelletsDAM
GenericNylon 6DAM
Material StatusPreliminary DataDAM
Part Marking Code>PA6-GF35<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA6DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
 SHIELD Technology ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA6-GF35ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAutomotive ApplicationsDAM
 Automotive Under the HoodDAM
 High Temperature ApplicationsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-46755.html

免责声明: 本文 DuPont Performance Polymers Zytel® PLUS PLS93G35DH1 BK261 Nylon 6 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4