- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.21
- 吸水率 [%]: 0.8
- 拉伸强度 [MPa]: 39.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 - 1.44 g/cc | 0.0437 - 0.0520 lb/in³ | Average value: 1.32 g/cc Grade Count:6 |
| Water Absorption | 0.800 - 1.20 % | 0.800 - 1.20 % | Average value: 1.05 % Grade Count:4 |
| Melt Flow | 5.00 - 70.8 g/10 min | 5.00 - 70.8 g/10 min | Average value: 37.9 g/10 min Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 39.0 - 52.0 MPa | 5660 - 7540 psi | Average value: 46.5 MPa Grade Count:6 |
| Elongation at Break | 18.0 - 32.0 % | 18.0 - 32.0 % | Average value: 22.8 % Grade Count:6 |
| Elongation at Yield | 4.00 - 10.0 % | 4.00 - 10.0 % | Average value: 6.25 % Grade Count:6 |
| Modulus of Elasticity | 1.60 - 3.64 GPa | 232 - 528 ksi | Average value: 2.37 GPa Grade Count:6 |
| Charpy Impact Unnotched | 3.80 - 17.0 J/cm² | 18.1 - 80.9 ft-lb/in² | Average value: 10.1 J/cm² Grade Count:6 |
| 4.45 - 7.60 J/cm² @Temperature -30.0 - 30.0 °C | 21.2 - 36.2 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 5.68 J/cm² Grade Count:6 | |
| Charpy Impact, Notched | 0.420 - 0.560 J/cm² | 2.00 - 2.67 ft-lb/in² | Average value: 0.490 J/cm² Grade Count:6 |
| 0.300 - 0.460 J/cm² @Temperature -30.0 - 30.0 °C | 1.43 - 2.19 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 0.380 J/cm² Grade Count:6 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | Average value: 1.00e+13 ohm-cm Grade Count:4 |
| Surface Resistance | 1.00e+12 - 1.00e+13 ohm | 1.00e+12 - 1.00e+13 ohm | Average value: 5.50e+12 ohm Grade Count:4 |
| Dielectric Strength | 35.0 - 40.0 kV/mm | 889 - 1020 kV/in | Average value: 37.5 kV/mm Grade Count:4 |
| Comparative Tracking Index | 600 V | 600 V | Average value: 600 V Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 60.0 - 140 µm/m-°C | 33.3 - 77.8 µin/in-°F | Average value: 97.5 µm/m-°C Grade Count:4 |
| Melting Point | 174 - 178 °C | 345 - 352 °F | Average value: 175 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 - 68.0 °C | 122 - 154 °F | Average value: 60.8 °C Grade Count:4 |
| Flammability, UL94 | HB | HB | Grade Count:6 |