- 熔体流动速率 [g/10min]: 11.3
- 密度 [g/cm3]: 1.01
- 拉伸强度 [MPa]: 47.0
- 热变形温度 [℃]: 135.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |
| Melt Flow | 11.3 g/10 min @Load 2.16 kg, Temperature 235 °C | 11.3 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 10 % | 10 % | 50 mm/min |
| Tensile Modulus | 1.52 GPa | 220 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 0.690 J/cm² | 3.28 ft-lb/in² | |
| 0.580 J/cm² @Temperature -30.0 °C | 2.76 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.00e+8 ohm-cm | 2.00e+8 ohm-cm | |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 174 °C | 345 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 138 °C | 280 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||