- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 1.0
- 拉伸强度 [MPa]: 25.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.50 % | 0.50 % | in normal climate 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | in water at 23°C; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 64.0 MPa | 9280 psi | value at 30 sec.; ISO 2039-1 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | v = 50 mm/min; ISO 527-2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-2 |
| Tensile Modulus | 0.400 GPa | 58.0 ksi | ISO 527-2 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | NB | NB | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz | 3.8 @Frequency 1e+6 Hz | IEC 60250 |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | in transformer oil; IEC 60243-1 |
| Comparative Tracking Index | 575 V | 575 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 171 °C | 340 °F | 10K/min; ISO 3146 |
| Maximum Service Temperature, Air | 75.0 °C | 167 °F | Long Term |
| 125 °C | 257 °F | Short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 - 165 °C | 257 - 329 °F | ISO 75-2 |