- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 1.5
- 拉伸强度 [MPa]: 40.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.5 % | 1.5 % | ISO 62 | ||
| Moisture Absorption | 0.700 % | 0.700 % | ISO 62 | ||
| Water Vapor Transmission | 8.00 g/m²/day | 0.515 g/100 in²/day | 23°C/85%r.h.; DIS 15106-1/-2 | ||
| Oxygen Transmission Rate | 350 cc/m²/day | 22.5 cc/100 in²/day | 23°C/0%r.h.; DIS 15105-1/-2 | ||
| 370 cc/m²/day | 23.8 cc/100 in²/day | 23°C/85%r.h.; DIS 15105-1/-2 | |||
| Carbon Dioxide Transmission | 1500 cc-mm/m²-24hr-atm | 3810 cc-mil/100 in²-24hr-atm | 23°C/0%r.h.; DIS 15105-1/-2 | ||
| 1600 cc-mm/m²-24hr-atm | 4060 cc-mil/100 in²-24hr-atm | 23°C/85%r.h.; DIS 15105-1/-2 | |||
| Melt Flow | 20 g/10 min | 20 g/10 min | (MVR) [cm³/10min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | conditioned; ISO 527-1/-2 | ||
| 50.0 MPa | 7250 psi | dry; ISO 527-1/-2 | |||
| Film Tensile Strength at Yield, MD | 35.0 MPa | 5080 psi | ISO 527-3 | ||
| Film Tensile Strength at Yield, TD | 35.0 MPa | 5080 psi | ISO 527-3 | ||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | dry; ISO 527-1/-2 | ||
| 45.0 MPa | 6530 psi | dry; ISO 527-1/-2 | |||
| Film Elongation at Break, MD | 850 % | 850 % | ISO 527-3 | ||
| Film Elongation at Break, TD | 900 % | 900 % | ISO 527-3 | ||
| Film Elongation at Yield, MD | 6.0 % | 6.0 % | ISO 527-3 | ||
| Film Elongation at Yield, TD | 6.0 % | 6.0 % | ISO 527-3 | ||
| Elongation at Break | >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | ||
| <= 50 % | <= 50 % | dry; ISO 527-1/-2 | |||
| Elongation at Yield | 10 % | 10 % | dry; ISO 527-1/-2 | ||
| 12 % | 12 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 1.10 GPa | 160 ksi | conditioned; ISO 527-1/-2 | ||
| 1.40 GPa | 203 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU | ||
| NB | NB | conditioned; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | conditioned; ISO 179/1eA | ||
| 0.700 J/cm² @Temperature 30.0 °C | 3.33 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Tear Strength | 20.0 kN/m | 114 pli | Trouser Tear resistance MD; ISO 6383-1 | ||
| 25.0 kN/m | 143 pli | Trouser Tear resistance TD; ISO 6383-1 | |||
| Elmendorf Tear Strength MD | 1020 g | 1020 g | ISO 6383-2 | ||
| Elmendorf Tear Strength TD | 1020 g | 1020 g | ISO 6383-2 | ||
| Film Tensile Strength at Break, MD | 80.0 MPa | 11600 psi | ISO 527-3 | ||
| Film Tensile Strength at Break, TD | 70.0 MPa | 10200 psi | ISO 527-3 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Optical Properties | Metric | English | Comments | ||
| Gloss | 150 % | 150 % | 60°; ISO 2813 | ||
| Descriptive Properties | |||||
| Food contact | EU Requirements | ||||
| FDA | |||||
| Form | Granules | ||||
| Gelboflextest [holes/m²], EMS | 1300 | ||||
| Industry & Consumer goods | Medical devices | ||||
| Medical | USP VI | ||||
| Packaging | Non oriented film | ||||
| Processing | Film Extrusion | ||||
| Injection Molding | |||||
| Other Extrusion | |||||
| Product Attributes | High viscosity | ||||