- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.1 % | 1.1 % | ISO 62 | ||
| Moisture Absorption | 0.600 % | 0.600 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 130 MPa | 18900 psi | conditioned; ISO 2039-1 | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | conditioned; ISO 527-1/-2 | ||
| 150 MPa | 21800 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 3.5 % | 3.5 % | dry; ISO 527-1/-2 | ||
| 4.0 % | 4.0 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 13.0 GPa | 1890 ksi | conditioned; ISO 527-1/-2 | ||
| 15.0 GPa | 2180 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | conditioned; ISO 179/1eU | ||
| 6.00 J/cm² @Temperature 30.0 °C | 28.6 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | conditioned; ISO 179/1eA | ||
| 0.800 J/cm² @Temperature 30.0 °C | 3.81 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | conditioned; IEC 60093 | ||
| Surface Resistance | 50 ohm | 50 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS | ||
| 150 °C | 302 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 125 °C | 257 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Electricals & Electronics | Mobile phones and other portable devices | ||||
| Form | Granules | ||||
| Industry & Consumer goods | Mechanical Engineering | ||||
| Medical devices | |||||
| Power transmission | |||||
| Sports & Leisure | |||||
| Tools & Accessories | |||||
| Processing | Injection Molding | ||||
| Special Characteristics | Anti-static | ||||
| High impact or impact modified | |||||
| Improved UV resistance (outdoor use) | |||||