- 密度 [g/cm3]: 1.02
- 拉伸强度 [MPa]: 31.0
- 热变形温度 [℃]: 115.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | |
| Moisture Absorption at Equilibrium | <= 0.50 % | <= 0.50 % | Humidity Absorption |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 28 % | 28 % | |
| Modulus of Elasticity | 0.580 GPa | 84.1 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | NB | NB | |
| 0.800 J/cm² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | |
| 10 @Frequency 100 Hz | 10 @Frequency 100 Hz | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | |
| Dissipation Factor | 0.11 @Frequency 1e+6 Hz | 0.11 @Frequency 1e+6 Hz | |
| 0.19 @Frequency 100 Hz | 0.19 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | |
| Vicat Softening Point | 130 °C | 266 °F | 50°C/hr/50 N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||