- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 1.3
- 热变形温度 [℃]: 175.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.50 % @Thickness 1.00 mm, Temperature 23.0 °C | 0.50 % @Thickness 0.0394 in, Temperature 73.4 °F | 50% R.H.; ISO 62 | ||
| Water Absorption at Saturation | 1.3 % @Thickness 1.00 mm | 1.3 % @Thickness 0.0394 in | ISO 62 | ||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/2 | ||
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-1/2 | ||
| Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527-1/2 | ||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| 7.00 J/cm² @Temperature -30.0 °C | 33.3 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.40 J/cm² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 100 V | 100 V | Test Solution A, 50 drops; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 150 µm/m-°C @Temperature 23.0 - 55.0 °C | 83.3 µin/in-°F @Temperature 73.4 - 131 °F | 45x15x10 mm; ISO 11359 | ||
| Melting Point | 178 °C | 352 °F | Peak Temperature; ISO 3146, ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75 | ||
| Vicat Softening Point | 175 °C | 347 °F | 10N; ISO 306 | ||
| 175 °C | 347 °F | 50N; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 Step | IEC 60426 | |||