- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 1.5
- 拉伸强度 [MPa]: 31.0
- 热变形温度 [℃]: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 1.5 % | 1.5 % | ISO 62 |
| Viscosity Test | 190 cm³/g | 190 cm³/g | Viscosity Number; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ISO 868 |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ISO 527-1, ISO 527-2 |
| Elongation at Break | >= 200 % | >= 200 % | ISO 527-1, ISO 527-2 |
| Elongation at Yield | 19 % | 19 % | ISO 527-1, ISO 527-2 |
| Tensile Modulus | 0.700 GPa | 102 ksi | ISO 527-1, ISO 527-2 |
| 50% Modulus | 0.0270 GPa | 3.92 ksi | ISO 527-1, ISO 527-2 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 3.30 J/cm² @Temperature 23.0 °C | 15.7 ft-lb/in² @Temperature 73.4 °F | Partial Break; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Spec.; IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | Spec.; IEC 60093 |
| Dielectric Constant | 4.6 @Frequency 1e+6 Hz | 4.6 @Frequency 1e+6 Hz | IEC 60250 |
| 7.4 @Frequency 100 Hz | 7.4 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.076 @Frequency 1e+6 Hz | 0.076 @Frequency 1e+6 Hz | IEC 60250 |
| 0.15 @Frequency 100 Hz | 0.15 @Frequency 100 Hz | IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 160 µm/m-°C @Temperature 23.0 - 55.0 °C | 88.9 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 |
| CTE, linear, Transverse to Flow | 160 µm/m-°C @Temperature 23.0 - 55.0 °C | 88.9 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | ISO 75-1 |
| Vicat Softening Point | 130 °C | 266 °F | 50N; ISO 306 |
| 170 °C | 338 °F | 10N; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |