- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 1.5
- 拉伸强度 [MPa]: 36.0
- 热变形温度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.50 % @Thickness 1.00 mm, Temperature 23.0 °C | 0.50 % @Thickness 0.0394 in, Temperature 73.4 °F | 50% R.H.; ISO 62 |
| Water Absorption at Saturation | 1.5 % @Thickness 1.00 mm | 1.5 % @Thickness 0.0394 in | ISO 62 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527-1/2 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ISO 527-1/2 |
| Elongation at Break | 42 % | 42 % | ISO 527-1/2 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527-1/2 |
| Tensile Modulus | 1.25 GPa | 181 ksi | ISO 527-1/2 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | Partial Break; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 100000 ohm-cm | 100000 ohm-cm | IEC 60093 |
| Insulation Resistance | 100000 ohm | 100000 ohm | Isolation Resistance (ROE DIN 43582:1983/VDE 0303 part 3; IEC 60167 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 180 µm/m-°C @Temperature 23.0 - 55.0 °C | 100 µin/in-°F @Temperature 73.4 - 131 °F | 45x15x10 mm; ISO 11359 |
| Melting Point | 178 °C | 352 °F | Peak Temperature; ISO 3146, ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 |
| Vicat Softening Point | 140 °C | 284 °F | 50N; ISO 306 |
| 175 °C | 347 °F | 10N; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||