- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 1.4
- 缺口冲击强度: 10.0
- 拉伸强度 [MPa]: 100.0
- 弯曲模量 [MPa]: 5.00
- 热变形温度 [℃]: 177.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 1.4 % | 1.4 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 175 °C | 347 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |