- 密度 [g/cm3]: 1.09
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 37.0
- 弯曲模量 [MPa]: 1.30
- 热变形温度 [℃]: 134.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.011 cm/cm @Time 86400 sec | 0.0090 - 0.011 in/in @Time 24.0 hour | ASTM D955 |
| 0.010 cm/cm @Time 86400 sec | 0.010 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.018 - 0.020 cm/cm @Time 86400 sec | 0.018 - 0.020 in/in @Time 24.0 hour | ASTM D955 |
| 0.019 cm/cm @Time 86400 sec | 0.019 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D638 |
| 36.0 MPa | 5220 psi | ISO 527 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ASTM D638 |
| 38.0 MPa | 5510 psi | ISO 527 | |
| Elongation at Break | 23.9 % | 23.9 % | ASTM D638 |
| 32.9 % | 32.9 % | ISO 527 | |
| Elongation at Yield | 17.5 % | 17.5 % | ASTM D638 |
| 18.4 % | 18.4 % | ISO 527 | |
| Tensile Modulus | 1.37 GPa | 199 ksi | 50 mm/min; ASTM D638 |
| 1.58 GPa | 229 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ISO 178 |
| 1.37 GPa | 199 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.83 J/cm | 12.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.23 | 0.23 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.14 | 0.14 | ASTM D3702 Modified |
| K (wear) Factor | 26.2 x 10-8 mm³/N-M | 13.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 112 µm/m-°C @Temperature -40.0 - 40.0 °C | 62.2 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 113 µm/m-°C @Temperature -40.0 - 40.0 °C | 62.8 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 108 µm/m-°C @Temperature -40.0 - 40.0 °C | 60.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 108 µm/m-°C @Temperature -40.0 - 40.0 °C | 60.0 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 150 °C @Thickness 3.20 mm | 302 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 146 °C @Thickness 3.20 mm | 295 °F @Thickness 0.126 in | unannealed; ASTM D648 | |