- 密度 [g/cm3]: 1.38
- 缺口冲击强度: 1.46
- 拉伸强度 [MPa]: 125.0
- 断裂伸长率 [%]: 178
- 弯曲模量 [MPa]: 7.51
- 热变形温度 [℃]: 177.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.220 % | 0.220 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec | 0.0070 - 0.0090 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 |
| 129 MPa | 18700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 125 MPa | 18100 psi | Type I, 5 mm/min; ASTM D638 |
| 129 MPa | 18700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 9.06 GPa | 1310 ksi | 50 mm/min; ASTM D638 |
| 9.07 GPa | 1320 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 176 MPa | 25500 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| 191 MPa | 27700 psi | ISO 178 | |
| Flexural Yield Strength | 178 MPa | 25800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.51 GPa | 1090 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.92 GPa | 1150 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.46 J/cm | 2.74 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.0 J/cm | 18.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C | 6.64 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.67 | 0.67 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 27.5 µm/m-°C @Temperature -30.0 - 30.0 °C | 15.3 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 44.4 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 177 °C @Thickness 3.20 mm | 351 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 169 °C | 336 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 172 °C @Thickness 3.20 mm | 342 °F @Thickness 0.126 in | unannealed; ASTM D648 | |