- 密度 [g/cm3]: 1.24
- 缺口冲击强度: 1.49
- 弯曲模量 [MPa]: 5.86
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
1.243 g/cc | 0.04491 lb/in³ | ASTM D792 | |
Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
0.220 % | 0.220 % | 23°C / 50% RH; ISO 62 | |
Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Time 86400 sec | 0.0020 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
0.0021 - 0.0030 cm/cm @Time 86400 sec | 0.0021 - 0.0030 in/in @Time 24.0 hour | ISO 294 | |
Linear Mold Shrinkage, Transverse | 0.0070 - 0.0080 cm/cm @Time 86400 sec | 0.0070 - 0.0080 in/in @Time 24.0 hour | ASTM D955 |
0.0074 - 0.0081 cm/cm @Time 86400 sec | 0.0074 - 0.0081 in/in @Time 24.0 hour | ISO 294 | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 106 MPa | 15400 psi | ASTM D638 |
108 MPa | 15700 psi | ISO 527 | |
Elongation at Break | 4.6 % | 4.6 % | ISO 527 |
4.7 % | 4.7 % | ASTM D638 | |
Tensile Modulus | 6.55 GPa | 950 ksi | 50 mm/min; ASTM D638 |
6.58 GPa | 954 ksi | 1 mm/min; ISO 527 | |
Flexural Strength | 169 MPa | 24500 psi | ISO 178 |
170 MPa | 24700 psi | ASTM D790 | |
Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
6.24 GPa | 905 ksi | ISO 178 | |
Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
Izod Impact, Unnotched | 9.50 J/cm | 17.8 ft-lb/in | ASTM D4812 |
Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1U |
Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 43.7 µm/m-°C @Temperature -40.0 - 40.0 °C | 24.3 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
43.7 µm/m-°C @Temperature -40.0 - 40.0 °C | 24.3 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
CTE, linear, Transverse to Flow | 112 µm/m-°C @Temperature -40.0 - 40.0 °C | 62.2 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
113 µm/m-°C @Temperature -40.0 - 40.0 °C | 62.8 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
163 °C @Thickness 3.20 mm | 325 °F @Thickness 0.126 in | unannealed; ASTM D648 |