- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.7
- 拉伸强度 [MPa]: 48.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | |
| Water Absorption | 1.7 % | 1.7 % | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min |
| Elongation at Break | 27 % | 27 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 2.23 GPa | 323 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| 14.2 J/cm² @Temperature -30.0 °C | 67.6 ft-lb/in² @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | |
| 0.420 J/cm² @Temperature -30.0 °C | 2.00 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 183 °C | 361 °F | 10°C/min |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||